PERLAKUAN PANAS

(HEAT TERATMENT). PERLAKUAN PANAS. Perlakuan panas (Heat Treatment) :.

keefe
Download Presentation

PERLAKUAN PANAS

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. (HEAT TERATMENT) PERLAKUAN PANAS

  2. Perlakuanpanas(Heat Treatment) : Adalahsuatuistilah yang menjelaskansuatuoperasiataukombinasi/gabunganoperasi yang melibatkanpemanasandanpendingnginan yang terkontrolterhadapsuatulogamataupaduanlogamdalamkeadaanpadatanuntuktujuanmemodifikasistrukturmikrosehinggadiperolehperubahansifat-sifatnya (terutamasifatmekanis) sesuai yang diinginkan.

  3. Menurut The International Federation For the Heat Treatment of Materials (IFHT) : Dalamperlakuanpanastidaksematahanyamelibatkanpemanasandanpengontrolankecepatanpendinginanpadapaduanlogam, Tetapitermasuk pula didalamnyaadalahpemberianataupenambahan atom lain melaluipermukaanlogam, sebagaimana yang terjadipada carburizing ataunitridingdanpemberian yang terjadipada controlled rolling dalam thermo mechanical treatment.

  4. TujuanUtamaPerlakuanPanasadalahsbb : • Memperlunak (to soften) yaitu : memperbaikisifatplastisitasdengancaramengaturukuran, bentukdandistribusimikrokonstituennya (fasaataubutiran), sertakeberadaandislokasididalambutiran.

  5. 2. Menghilangkantegangansisa (to stress relieve) yaitu : Memungkinkanberlangsungnyarelaksasitegangan-tegangansisadengancarameningkatkantemperatur (memanaskan) sehinggadiperolehpenurunankekuatanluluh (yield strength) danmeningkatkan recovery.

  6. Melakukanhomogenisasi (to homogenize) yaitu : mendapatkankomposisikimia yang homogendidausilambutiran (grain) melaluidifusiunsur-unsur yang adadalampaduanlogampadatemparaturtinggi, seperti : austenizing

  7. Meningkatkanketangguhaan • Memperkeras • Menambahunsurkimia • Meningkatkansifatfisik.

  8. Secaragarisbesarperlakuanpanasdikelompokkansbb: • Proses annealing: a. Full annealing b. Spheroidizing c. Isothermal anealing d. dll.

  9. 2. Normalizing 3. Hardening process : a. water, oil ataudaradan tempering b. Time quenching dan tempering c. isothermal guenchingdan tempering d. Austempering e. Martempering

  10. 4. Other Hardening process: a. Precipitation hardening (age hardening) b. Dispersion hardening c. Thermommechaanical treatment 5. Thermal surface hardening a. flame hardening b. Inducction hardening c. Electron beam hardening

  11. 6. Diffusion treatment lainnya : a. Siliconizing b. Chromizing c. Boronizing d. Carburizing e. Aluminizing

  12. Dalam precipitation hardening : transformasifasa yang terlibatdalamkeadaanpadatan, umumnyaberlangsungmelaluipergerakan atom, yaitusaatberlangsungnyaprosespengintiandanpertumbuhanpartikelendapan.

  13. Quench hardening yang memunculkanfasamartensit, transformasifasa yang berlangsungtanpapergerakan atom, yaitumelaluiprosespergeseranbidangkristal yang menyebabkandistorsikisi. (prosestransformasiberlangsungsangatcepat 10 -2 detik)

  14. FULL ANEALING Full anaelingbertujuanuntukmelunakkan, mengurangitegngansisa, merubahsifatmekanisdanmendapatkanstrukturmikro yang homogen. Pemanasandilakukankira-kira 40 C diatas Ac3. Pemanasanbajapadatemperaturdidaerahkestabilanfasaaustenitiniakanmenyebabkantransformasifasadarikeadaanawal : ferit + Perlituntukbajahipoeutektoid

  15. Perlit : untukbajaeutektoid Ferit + Cementite : untukbajaHipereutektoid Transformasifasadarimenjadi Austenite berlangsungmelaluiprosespengintiandanpertumbuhaanbutir austenite. Semakin lama pemanasansedikitdiatas Ac3 akanmenghasilkanbutiranaustenit yang lebihbesar.

  16. HOMOGENISASI (homogenize annealing) Tujuandariperlakuanpanasiniadalah : untukmendapatkanhomogenisasikomposisikimiadarisuatupaduanlogam (terutamabajadalambentuk ingot) hasildariprosespengecoran. Temperaturperlakuanpanas yang digunakanadalah 1100 C untukmenghindariretakanterutamauntukbenda yang berdimensitipis.

  17. Pemanasanpadatemperaturhomogenisasidilakukanrelatif lama untukmemungkinkanjarakdifusi atom-atom yang tersegresidaribatasbutirankepusatbutiranatausebaliknya.

  18. SPERERODISASI Strukturspherodizedadalahstrukturmikrobajadengansementitmemilikimorfologimembulat (sphere) bukandalambentuk plat sepertiperlit. Sehingga ductility lebihbesarsehinggamachinibilitymeningkat Umumnyadilakukanpadabajakarbonrendahsampaisedang.

  19. Anealingumumnyaditerapkankepadapaduanlogam yang telahmengalamipengerjaandingin (cold working) dengantujuan : untukmelunakkankembalipaduanlogamdarikeadaanpengerasanregangan (strain hardening) Batas antarapengerjaandingindenganpengerjaanpanasadalah : TemperaturREKRISTALISI

  20. Temperaturrekritalisasi (T rek) adalah : Temperatur minimum yang memungkinkanterjadinyapengintiankristal-kristalbarudarikristal-kristal yang telahmengalamideformasiplastis. Prosesrekristalisasiberlangsungpadatempereatur yang relatiftinggi. Harga T rektergantungpada : - komposisikimiapaduan - kecepatandanbesarnyadeformasiplastis.