Background for AA8006

Background for AA8006. AA8006-O surfaces, as-received or etched, activate by annealing at lower temperatures (350 C) than model binary AlPb alloys Activation is actually reduced by increasing the annealing temperature (Yann) Role of grain size on activation not investigated.

keena
Download Presentation

Background for AA8006

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Background for AA8006 • AA8006-O surfaces, as-received or etched, activate by annealing at lower temperatures (350 C) than model binary AlPb alloys • Activation is actually reduced by increasing the annealing temperature (Yann) • Role of grain size on activation not investigated

  2. Anodic behavior of alloy 8006 as function of annealing temperature Potential, VSCE Current Density, mA/cm2

  3. Potential, VSCE Current Density, mA/cm2 Anodic polarization behaviour of etched AA8006 (10s etched in 5% NaOH solution and 60s desmutted in HNO3), then annealed at different temperatures, as compared with that of the annealed AlPb20 model alloy.

  4. Initial results from TEM characterizations The elongated primary particles, parallel the rolling direction below the surface region