20 likes | 169 Views
( a). ( b). ( a). ( b). Figure 1. FGM samples with ( a) a crack and (b) camber.
E N D
(a) (b) (a) (b) Figure 1. FGM samples with (a) a crack and (b) camber Figure 2 (a) particle size distribution for each powder and (b) Diameter of sintered samples with varying powder composition, the powder composition located between two blue lines have the potential to achieve similar final dimension Figure 3. Punch used to produce occlusive interface between powder layers (a) (b) Figure 4. (a) The shrinkage rate and (b) densification rates can be seen to be similar for all three layers Innovative Process • 1. Manipulated powder mixture: • Two alumina powder and two zirconia powder were mixed to manipulate material properties of powder mixture • Sintered dimension similarity could be obtained for the three layers • Possible to eliminate cracks and camber Fabrication of Alumina/Zirconia Functionally Graded Materials (FGM) Adam Sneller, Li Sun Advisor: Dr. Patrick Kwon • Background: • A functionally graded material features a concentration gradient • the proportion each material varies throughout the object • Useful for circumstances when remote parts of an object are • exposed to different conditions • 2. Design of Interface: • Three different interfaces were investigated: • Natural – created using flat punch • Smooth – created by pressing powder with a flat punch, then rotating to make surface smoother • 3. Occlusive – created using the punch shown in Fig. 3 • – A quasi-continuous shift from one layer to the next is possible • Objective: • Create a 3-layered FGM made of alumina and zirconia powders: • Pure zirconia (Layer Z) • Half zirconia, half alumina (Layer M) • Pure alumina (Layer A) 3.Optimized compaction load and temperature changing rate See Table 1 • Problem: • Cracks form between layers • The entire object warps in shape (camber) Table 1. Optimized parameters to achieve a flat 3-layer Al2O3/ZrO2 FGM without cracks Final Solution with Transient Sintering Behavior Analysis • Reason: • During sintering, thermal reactions may differ between layers • Mismatch in densification rate • Mismatch in thermal expansion • Results in residual stress which causes cracks or camber • Unavoidable in using only one powder for each layer • The transient sintering behaviors of three chosen powder mixtures under optimized experimental condition are almost same. • This similarity ensures that no large dimension mismatch could occur at any time during sintering • References • Cai, P.Z., et al. 1997. “Constrained densification of alumina/zirconia hybrid laminates, I: experimental observations of processing defects,” J. Am. Ceram. Soc., 80(8): 1929–1939. • 2. Torrecillas, R., et al. 2000. “Functionally graded zircon-molybdenum materials without residual stresses,” J. Am. Ceram. Soc., 83(2): 454–456. • 3. Lance, D., et al. 2004. “Correlation between densification rate and microstructural evolution for pure alpha alumina,” J. Eur. Ceram. Soc., 24(9): 2749–2761