1 / 24

Quantum Enabling Technology Materials Research for Superconducting Quantum Computing

Quantum Enabling Technology Materials Research for Superconducting Quantum Computing. Materials P.I. - D. P. Pappas Affiliates: Jeff Kline Fabio da Silva Students: Will Kindel Teresa Osminer Postdocs *David Wisbee. Anatomy of a superconducting qubit. Wiring. Top electrode.

monte
Download Presentation

Quantum Enabling Technology Materials Research for Superconducting Quantum Computing

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Quantum Enabling TechnologyMaterials Research for Superconducting Quantum Computing Materials P.I. - D. P. Pappas Affiliates: Jeff Kline Fabio da Silva Students: Will Kindel Teresa Osminer Postdocs *David Wisbee

  2. Anatomy of a superconducting qubit Wiring Top electrode Insulator Junction - Tunnel barrier Bottom electrode Insulator (if subs. conductive) Substrate

  3. Materials development – can we reduce decoherence? Al a-SiOx Absorption in dielectric & junction (a-SiO2) & (a-AlO2) AlOx Si • Focus on: • Insulators: along traces & around junction • in substrate • crossovers • Tunnel barrier: Between top and bottom electrode • Electrode surfaces: Flux noise from surface spins

  4. Resonant circuits have low Q at low T, P => With & without SiO2 over the capacitor C/2 C/2 L Dissipation is in SiO2 dielectric of the capacitor! ~Pout

  5. Qubit spectroscopysplittings due to two-level systems in Junction tunnel barrier • Increase the bias voltage (tilt) • Frequency of |0> => |1> transition goes down Increase bias Resonances

  6. DC SQUIDs: SF1/2(1Hz) vs. T Loop materials: Nb (A1-4, F1) Pb (C2) PbIn (A5, B1, C1, E1,2) Loop effective areas: 1,400 mm2– 200,000 mm2 ( At low T: SF1/2(1Hz) ≈ 7 ± 3 mF0Hz-1/2 Wellstood, Urbina and Clarke (1987)

  7. Superconducting JJ qubits – mtls. & meas. Primary NIST differentiator – Crystalline junction material Secondary differentiator – Crystalline bottom electrodes UHV & processing combination Enabling development: Substrate preparation Development of low loss insulators priority – a-Si:H, a-C:H, Si(111) Benchmarks – a-SiOx, a-SiN Facilities ADR with I/V and RF capablility RF capability on PPMS

  8. Original Statement of Work Tasks: • Substrate preparation • Bottom electrode • Epitaxial barrier development • Top Electrode • Dielectric layers • Top & bottom wiring layers

  9. Progress Studied substrates from different vendors ( collaboration w/LL, DARPA) - Task 1 Obtained 3” wafers of Sapphire (0001) Measured roughness using AFM Developed Qubit test platform for junction tests - Task 1-6 12 qubit test die – quickly find optimized junctions Devices fabricated here Measurements done– 500 ns T1!! Developed insulator test platform – Task 1-6 Make simple structure to test loss in various dielectrics – new set of dies Devices fabricated here Measurements show absorption – sent to JPL Fabricated SQUIDs and measure noise – Task 1-6 Various widths & flux trapping conditions Fabricated Ru capped washers Added Fe Measured - Same noise level with Ru as Al & Re, reduced by factor of 2 0.2 ML Fe Measure junctions in-house for quality control – Task 1-6 ADR test facility built up – Tested first junctions here last week Commissioned 3” chamber for epi Si(111)/Al(111)/Al2O3/Al(111) - Task 1-4

  10. Task 1 - Wafer substrate AFM analysis • Acquired wafers from 3 manufacturers • Epi-stone (ES) & Saint Gobain (SG), and Crystal GmbH (CG) • Conducted AFM on them in collaboration with LL under DARPA • CG & ES wafers looked best – show atomic steps • SG wafer surface looked poor, lots of scratches, no steps. CG wafer surface ES wafer surface SG wafer surface Note – Growth of Re on SG wafers actually show the best RHEED!

  11. Progress Studied substrates from different vendors ( collaboration w/LL, DARPA) - Task 1 Obtained 3” wafers of Sapphire (0001) Measured roughness using AFM Developed Qubit test platform for junction tests - Task 1-6 12 qubit test die – quickly find optimized junctions Devices fabricated here Measurements done– 500 ns T1!! Developed insulator test platform – Task 1-6 Make simple structure to test loss in various dielectrics – new set of dies Devices fabricated here Measurements show absorption – sent to JPL Fabricated SQUIDs and measure noise – Task 1-6 Various widths & flux trapping conditions Fabricated Ru capped washers Added Fe Measured - Same noise level with Ru as Al & Re, reduced by factor of 2 0.2 ML Fe Measure junctions in-house for quality control – Task 1-6 ADR test facility built up – Tested first junctions here last week Commissioned 3” chamber for epi Si(111)/Al(111)/Al2O3/Al(111) - Task 1-4

  12. Qubit loop Bias coil DC-SQUID Task 3 - 12 Qubit Die Layout Allows us to test a wide range of junction sizes even with low yield!

  13. Progress Studied substrates from different vendors ( collaboration w/LL, DARPA) - Task 1 Obtained 3” wafers of Sapphire (0001) Measured roughness using AFM Developed Qubit test platform for junction tests - Task 1-6 12 qubit test die – quickly find optimized junctions Devices fabricated here Measurements done– 500 ns T1!! Developed insulator test platform – Task 1-6 Make simple structure to test loss in various dielectrics – new set of dies Devices fabricated here Measurements show absorption – sent to JPL Fabricated SQUIDs and measure noise – Task 1-6 Various widths & flux trapping conditions Fabricated Ru capped washers Added Fe Measured - Same noise level with Ru as Al & Re, reduced by factor of 2 0.2 ML Fe Measure junctions in-house for quality control – Task 1-6 ADR test facility built up – Tested first junctions here last week Commissioned 3” chamber for epi Si(111)/Al(111)/Al2O3/Al(111) - Task 1-4

  14. Task 5 - Quantum Materials: Low loss insulators Test platform do develop low loss insulators • Collaborating with Ben Mazin to design antenna test platform • Measurements made on a-SiOx as a reference Q ~ 1000 • Just started making measurments on a-ALD-AlOx, • While measurements in progress, preparing SiN, a-C, a-Ge

  15. Progress Studied substrates from different vendors ( collaboration w/LL, DARPA) - Task 1 Obtained 3” wafers of Sapphire (0001) Measured roughness using AFM Developed Qubit test platform for junction tests - Task 1-6 12 qubit test die – quickly find optimized junctions Devices fabricated here Measurements done– 500 ns T1!! Developed insulator test platform – Task 1-6 Make simple structure to test loss in various dielectrics – new set of dies Devices fabricated here Measurements show absorption – sent to JPL Fabricated SQUIDs and measure noise – Task 1-6 Various widths & flux trapping conditions Fabricated Ru capped washers Added Fe Measured - Same noise level with Ru as Al & Re, reduced by factor of 2 0.2 ML Fe Measure junctions in-house for quality control – Task 1-6 ADR test facility built up – Tested first junctions here last week Commissioned 3” chamber for epi Si(111)/Al(111)/Al2O3/Al(111) - Task 1-4

  16. Task 6 - Flux noise vs. F on Ru capped Al with 0.2 ML Fe on top Red curve – SQUID washer w/ Ru cap Blue Curve – Same SQUID washer w/ Ru cap + 0.2 ML Fe on top Factor of 2 reduction in noise due to Fe!! (rather than increasing noise)

  17. Progress Studied substrates from different vendors ( collaboration w/LL, DARPA) - Task 1 Obtained 3” wafers of Sapphire (0001) Measured roughness using AFM Developed Qubit test platform for junction tests - Task 1-6 12 qubit test die – quickly find optimized junctions Devices fabricated here Measurements done– 500 ns T1!! Developed insulator test platform – Task 1-6 Make simple structure to test loss in various dielectrics – new set of dies Devices fabricated here Measurements show absorption – sent to JPL Fabricated SQUIDs and measure noise – Task 1-6 Various widths & flux trapping conditions Fabricated Ru capped washers Added Fe Measured - Same noise level with Ru as Al & Re, reduced by factor of 2 0.2 ML Fe Measure junctions in-house for quality control – Task 1-6 ADR test facility built up – Tested first junctions here last week Commissioned 3” chamber for epi Si(111)/Al(111)/Al2O3/Al(111) - Task 1-4

  18. I-V curve from epitaxial barrier

  19. Results of our junctions: R (1/G) vs. T for Al/AlOx/Al tunnel jctn. • Signatures of quantum tunneling • R increases as T decreases • Zero slope at low T In collaboration with Oh et al (Rutgers) Zero-bias resistance

  20. Progress Studied substrates from different vendors ( collaboration w/LL, DARPA) - Task 1 Obtained 3” wafers of Sapphire (0001) Measured roughness using AFM Developed Qubit test platform for junction tests - Task 1-6 12 qubit test die – quickly find optimized junctions Devices fabricated here Measurements done– 500 ns T1!! Developed insulator test platform – Task 1-6 Make simple structure to test loss in various dielectrics – new set of dies Devices fabricated here Measurements show absorption – sent to JPL Fabricated SQUIDs and measure noise – Task 1-6 Various widths & flux trapping conditions Fabricated Ru capped washers Added Fe Measured - Same noise level with Ru as Al & Re, reduced by factor of 2 0.2 ML Fe Measure junctions in-house for quality control – Task 1-6 ADR test facility built up – Tested first junctions here last week Commissioned 3” chamber for epi Si(111)/Al(111)/Al2O3/Al(111) - Task 1-4

  21. Lesker 3” deposition chamber

  22. Note: Test devices include all/most layers=> Hard to separate original tasks! • Re-parse SOW Tasks to reflect project goals. • Substrate preparation • Bottom electrode • Epitaxial barrier dev. • Top Electrode • Dielectric layers • Top & bottom wiring • Understand tunneling process • Devices on alternative substrates • Develop high Q circuits • Study noise in devices • Test coherence advances • Still the same scope of work. • Allows us to make Gantt chart directly from SOW.

  23. Detailed subtasks • Understand tunnel process in epi-barriers • Tool up to measure I-V curves in-house with ADR • Measurement of samples at low temperature • Reduce spectroscopy splitting further using different tunnel barriers • Study materials doping in barriers • Study device/junction failure • Develop alternative substrates • Research & indentify new systems • Tool up 3” chamber in clean room for identified system • Prepare substrates • Prepare bottom electrode • Prepare barriers • Prepare top electrode • Fabricate into test junctions • Develop high Q materials for low T, P applications • Tool up for measurements at 1.7 K and 60 mK • Fabricate L-C circuits & test with SiO2 • Tool up to grow a-Si dielectrics • Investigate new materials • Complete work with antenna resonators • Study noise due to surfaces & interfaces • Fabrication of SQUID devices • Identify source of decoherence loss • Test Coherence advances • Fabricate 12 qubit dies using optimal materials from above • Integrate & optimize all improvements into single qubit & measure

  24. Gantt Chart