Cu, Typ: A1, Raumgruppe: Fm3m

Cu, Typ: A1, Raumgruppe: Fm3m. Atomlagen (Wyckoff): Cu: 4a (0,0,0) Beispiele II a: Ca, Sr III a: Al IV a: Pb VIII: Ne, Ar, Kr, Xe (4K) I b: Cu, Ag, Au VIII b: Rh, Ir, Ni, Pd, Pt La: Ce, Yb Ac: Th. Cu, Typ: A1, Raumgruppe: Fm3m. [001] 4/m. [110] 2/m. Kubisch Flächenzentriert.

nona
Download Presentation

Cu, Typ: A1, Raumgruppe: Fm3m

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Cu, Typ: A1, Raumgruppe: Fm3m Atomlagen (Wyckoff): Cu: 4a (0,0,0) Beispiele II a: Ca, Sr III a: Al IV a: Pb VIII: Ne, Ar, Kr, Xe (4K) I b: Cu, Ag, Au VIII b: Rh, Ir, Ni, Pd, Pt La: Ce, Yb Ac: Th

  2. Cu, Typ: A1, Raumgruppe: Fm3m [001] 4/m [110] 2/m Kubisch Flächenzentriert [111] -3

  3. W, Typ: A2, Raumgruppe: Im3m Atomlagen (Wyckoff): W: 2a (0,0,0) Beispiele I a: Li (78K); Na, K, Rb, Cs (5K) II a: Ba IV b: Ti (T > 882°C) V b: V, Nb, Ta VI b: Cr, Mo, W VIII b: Fe La: Eu

  4. W, Typ: A2, Raumgruppe: Im3m [111] -3 [001] 4/m [110] 2/m Kubisch Innenzentriert (Raumzentriert)

  5. Mg, Typ: A3, Raumgruppe: P63/mmc Hexagonal dichteste Kugelpackung Atomlagen (Wyckoff): Mg: 2c (1/3, 2/3, 1/4) Beispiele I a: H (4K) II a: Be, Mg III a: Tl II b: Zn, Cd III b: Sc, Y IV b: Ti (T < 882°C), Zr, Hf VII b: Tc, Re VIII b: Ru, Os, Co La: Gd, Tb, Dy, Ho, Er, Tm, Lu

  6. Mg, Typ: A3, Raumgruppe: P63/mmc [001] 63/m [100] 2/m [110] 2/c Hexagonal Primitiv

  7. Dichteste Kugelpackung Kubisch Hexagonal B A A C B B A A Richtung 111 Richtung 001

  8. Dichteste Kugelpackung

  9. Phasenübergänge kubisch  hexagonal Kubisch Hexagonal Co: Fm3m unterhalb von 690 K (417°C) Ni: Fm3m Ti: Im3m oberhalb von 1155 K (882°C) Co: P63/mmc oberhalb von 690 K (417°C) Ni: P63/mmc in dünnen Schichten Ti: P63/mmc unterhalb von 1155 K (882°C)

  10. C, Typ: A4, Raumgruppe: Fd3m Diamantstruktur Atomlagen (Wyckoff): C: 8a (0,0,0) Beispiele C (Diamant) Ge, Si, Sn (Halbleiter)

  11. C, Typ: A4, Raumgruppe: Fd3m [111] -3 [001] 41/d [110] 2/m Kubisch Flächenzentriert

  12. C, Typ: A9, Raumgruppe: P63mc Hexagonal Primitiv Graphitstruktur Atomlagen (Wyckoff): C: 2a (0,0,0) und 2b (1/3, 2/3, 0)

  13. C, Typ: A9, Raumgruppe: P63/mmc Graphit – Polymorphe Struktur Atomlagen (Wyckoff): C: 2b (0, 0, ¼) und 2b (1/3, 2/3, ¼) Hexagonal Primitiv

  14. NaCl, Typ: B1, Raumgruppe: Fm3m Steinsalz Atomlagen (Wyckoff): Na: 4a (0,0,0) Cl: 4b (½, ½, ½) Beispiele Carbide und Nitride der Übergangsmetalle (IV b, V b und VI b): TiC, TiN, ZrC, ZrN, HfC, HfN, VC, VN, NbC, NbN, TaC, TaN, CrN, Cr23C6 UN

  15. NaCl, Typ: B1, Raumgruppe: Fm3m [001] 4/m [110] 2/m [111] -3 Kubisch Flächenzentriert