LDC borstplätering. LDC Portable Electroplating Cold process: used at room temperature , no stress or adjustments because of termal distorsion. To tolerance : normally no machining required Quick metal build-up: 0,05 mm in 10-15 min.
E N D
LDC borstplätering LDC Portable Electroplating Cold process: used at roomtemperature, no stress or adjustmentsbecause of termal distorsion. To tolerance: normally no machiningrequired Quick metal build-up: 0,05 mm in 10-15 min. Plating: on all conductive materials, castiron, stainless, mild steel, copper, chromeetc Densedeposits: no or verylittleporosity in mostcoatings Many differens metals: nickel, gold, silver, copper, cobolt, zinc and alloys. Excellent bonding: molecular bonding results in very god adhesion, all coatingscan be machined, ground or polished. Mobile equipment: the repair can be done on site www.ldc-brushplating.com
LDC borstpläteringTele: + 46 248 174 40 E-mail: ldc@swipnet.se On site repair of the crankshaft in a conversion press. www.ldc-brushplating.com
LDC borstplätering Tele: + 46 248 174 40 E-mail: ldc@swipnet.se Damaged /worn flywheel bearing areas on the crankshaft in a conversion press. www.ldc-brushplating.com
LDC borstpläteringTele: + 46 248 174 40 E-mail: ldc@swipnet.se Prepare and masking off surrounding areas. www.ldc-brushplating.com
LDC borstpläteringTele: + 46 248 174 40 E-mail: ldc@swipnet.se • Plating procedure going on . www.ldc-brushplating.com
LDC borstpläteringTele: + 46 248 174 40 E-mail: ldc@swipnet.se Damaged bearing journal plated to size. www.ldc-brushplating.com
LDC borstpläteringTele: + 46 248 174 40 E-mail: ldc@swipnet.se Crankshaft is finished and the original tolerances and measurements are obtained. Ready to assemble the flywheel . www.ldc-brushplating.com
LDC borstpläteringTele: + 46 248 174 40 E-mail: ldc@swipnet.se Repair on site . Lower bed die in a conversion press with local wear damages www.ldc-brushplating.com
LDC borstpläteringTele: + 46 248 174 40 E-mail: ldc@swipnet.se Plated/repaired damage on the lower bed die. LDC-2904 copper hi-speed HB250 were used to fill the damage up . Top coated with LDC-2807 Nickel acid for wear and corrosion protection. www.ldc-brushplating.com
LDC borstpläteringTele: + 46 248 174 40 E-mail: ldc@swipnet.se Repair on site . Lower bed die in a conversion press with local wear damages www.ldc-brushplating.com
LDC borstpläteringTele: + 46 248 174 40 E-mail: ldc@swipnet.se Damaged area in the lower bed die. www.ldc-brushplating.com
LDC borstpläteringTele: + 46 248 174 40 E-mail: ldc@swipnet.se One worn out slide. There are damages from the pistons and micro vibrations. And causes oil leaking. www.ldc-brushplating.com
LDC borstpläteringTele: + 46 248 174 40 E-mail: ldc@swipnet.se Damaged area inside the slide www.ldc-brushplating.com
LDC borstpläteringTele: + 46 248 174 40 E-mail: ldc@swipnet.se The damages is being plated with a hard copper of 250 Brinell and grinded to original tolerances. www.ldc-brushplating.com
LDC borstpläteringTele: + 46 248 174 40 E-mail: ldc@swipnet.se Area has now a new top coating with a nickel with a hardness of 400 brinell and also gives a excellent protection from new damages. www.ldc-brushplating.com
LDC borstpläteringTele: + 46 248 174 40 E-mail: ldc@swipnet.se Plating is now finished and the slide is ready for assembly. www.ldc-brushplating.com
LDC borstpläteringTele: + 46 248 174 40 E-mail: ldc@swipnet.se Oil leakage from scratched and damaged main pistons brush plated on site. www.ldc-brushplating.com