An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. 鐵粉芯材料簡介(Ferrite Material) 2005. 9.10 講師:chia ho

  2. 鐵粉芯材料 • 鐵粉芯為一種多元結晶體 (polycrystal) 、以高溫熔結 ( 1000 ~ 1400°C ) 之材料。 它有高電氣電阻之特性，故在高頻時之渦流損耗較小。 • 錳—鋅系列之鐵粉芯可用於數 MHz 之頻率，而鎳—鋅系列之鐵粉芯可用於數佰 MHz 之頻率。 • 經過不同的混合、燒結、研磨、粒狀成形及加壓成形等製程，可製成各種不同用途之鐵粉芯。 • 濾波器 — 低損耗、磁性穩定及高導磁率 • 信號變壓器 — 高飽和磁通密度及高導磁率 • 電源用變壓器 — 高飽和磁通密度及低電力損耗

  3. 導磁率 ( Permeability ; µ ) L l 9 i = • • 10 2 4  N A i =初始導磁率 L = 有效自感量 (H) N = 繞線圈數 l = 磁蕊內磁性路徑之平均長度 (cm) A = 磁蕊之切面積 (cm ) 2

  4. 有效導磁率 (Effective permeability ; µe) L l 9 e = •  • 10 2 4  N A l -1  = C1 = 磁蕊長常數 (cm ) A e =有效導磁率 L = 有效自感量 (H) N = 繞線圈數 l = 磁蕊內磁性路徑之平均長度 (cm) A = 磁蕊之切面積 (cm ) 2

  5. 增量 (Incremental) 導磁率 ( µ ) 和逆向 (Reversible) 導磁率 (µrev) B B = 增量磁通密度 ( 高斯 ; gauss ) µ = H H = 增量磁場強度 ( Oe ; oersted ) 逆向導磁率 ( µrev )是指交流磁場在振幅為零時，增量導磁率之界限值。它是直流磁通密度 B 之一個函數，且當 B = 0 時，其值最大，同時其值也隨 B 增加而減少。 由於磁通密度隨磁蕊的形狀及其間隙的大小而變，逆向導磁率不適用於如 E 型及P 型之磁蕊。