Window Coating Absorbance Spectra

Window Coating Absorbance Spectra. Lisa Pawlowicz 17 August 2010. Overview . Materials and Methods Absorbance of Substrates Absorbance due to In 2 O 3 (ITO) Absorbance due to MgO Topics for Further Investigation. Window Coatings. 1.22” diameter. 50 Å MgO. 45 Å In 2 O 3 (ITO).

tamasine-mitsuyama
Download Presentation

Window Coating Absorbance Spectra

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Window Coating Absorbance Spectra Lisa Pawlowicz 17 August 2010

  2. Overview • Materials and Methods • Absorbance of Substrates • Absorbance due to In2O3 (ITO) • Absorbance due to MgO • Topics for Further Investigation

  3. Window Coatings 1.22” diameter 50 Å MgO 45 Å In2O3 (ITO) .098” Borofloat (Sn doped on one side) .098” Fused Silica OR 45 Å In2O3 (ITO) 50 Å MgO • Windows cut by Oswald Siegmund at SSL • Coatings applied by Joe Libera at Argonne • coatings applied to one side but (likely) diffused onto both

  4. Absorbance Spectrum Scans A - absorbance I0 – intensity of incident light I – intensity of transmitted light α – attenuation coefficient x – optical path length (thickness) T - transmission • Measuring absolute absorbance: no scaling factor Absorbance scans done with a Hitachi U-3010 spectrophotometer: Instrument Parameters Measurement Type: Wavelength Scan Starting Wavelength: 800.00 nm Ending Wavelength: 200.00 nm Scan Speed: 300 nm/min Sampling Interval: 1.00 nm High Resolution Path Length: 2.0 mm (window thickness 2.5 mm) http://home.uevora.pt/~filmflc/GQS_Equipment_eng.htm

  5. , Absorbance of Substrate: 7980-2G Fused Silica Absorbance Wavelength http://rmico.com/technical-notes/transmission-curves

  6. , Absorbance of Substrate: Borofloat Absorbance Wavelength Wavelength http://www.pgo-online.com/intl/katalog/curves/boro_kurve.html

  7. , Absorbance of Substrates ---- Fused Silica ---- Borofloat Absorbance Wavelength • Conclusions: • caution required in UV range (Borofloat particularly a poor choice for wavelengths < 350 nm) • otherwise these substrates acceptable for the purposes of the LAPPD

  8. Absorbance due to ITO Multiple orientations of fused silica due to orientation dependent absorbance of coated window ---- Fused Silica (orientation #1) ---- Fused Silica (orientation #2) ---- Borofloat Absorbance Wavelength

  9. Absorbance due to ITO Transmission • no industry standard for ITO coatings • Conclusions: • ITO absorbance independent of substrate http://www.evaporatedcoatings.com/eci-949ar-ITOar.htm

  10. Absorbance due to MgO ---- Fused Silica (orientation #1) ---- Fused Silica (orientation #2) ---- Borofloat Absorbance Wavelength

  11. Absorbance due to MgO ---- Fused Silica (orientation #1) ---- Fused Silica (orientation #2) ---- Borofloat Absorbance Wavelength

  12. Absorbance due to MgO Transmission Spectrum of 1 nm thick MgO Transmission Bhattacharya, P., Das, R. R., and Katiyara, R. S. (2003). “Fabrication of stable wide-band-gap ZnOÕMgO multilayer thin films.” Applied Physics Letters, 83; 10. 2010-2012.

  13. Absorbance due to MgO ---- Fused Silica (orientation #1) ---- Fused Silica (orientation #2) peaks transitions across band gap Absorbance Energy

  14. Absorbance due to MgO 1 • 5-7 eV peak predicted by band structure • 2.75 eV peak • caused by interaction with substrate? ITO? • could enable unwanted interactions between conduction bands of adjacent layers e- EC EF EV Glass MgO Photocathode 1 Leone, R.M. (2006). Wide band gap engineering of magnesium oxide-zinc oxide II-VI semiconductors (Master’s dissertation, Northern Arizona University, 2006). http://www.physics.arizona.edu/~leone/dox/leone_thesis.pdf

  15. Absorbance due to MgO 1 • 5-7 eV peak predicted by band structure • 2.75 eV peak • caused by interaction with substrate? ITO? • could enable unwanted interactions between conduction bands of adjacent layers EC EF EV e- Glass MgO Photocathode 1 Leone, R.M. (2006). Wide band gap engineering of magnesium oxide-zinc oxide II-VI semiconductors (Master’s dissertation, Northern Arizona University, 2006). http://www.physics.arizona.edu/~leone/dox/leone_thesis.pdf

  16. Absorbance due to MgO • Conclusions: • MgO absorbance doesn’t match literature • MgO absorbance shows some dependence on substrate • Orientation dependence  implies uneven coating • Spectroscopic measurements necessary to ensure quality of samples • Interactions between layers could cause complications

  17. Topics for Further Investigation • Why is there a 2.75 eV peak in the MgO absorbance spectrum? • How do the 5 eV and 2.75 eV peaks in the MgO absorbance spectrum affect MgO’s functionality? • How would tempering the different materials affect their absorbance spectra? • How do absorbance spectra differ between batches of windows and films?