API 5CT/ISO 11960 Grades in NACE MR0175/ISO 15156 Pt. 2

API 5CT/ISO 11960 Grades in NACE MR0175/ISO 15156 Pt. 2. John W Martin. Listing of API 5CT/ISO 11960 Grades. Group 1 H40, J55, K55, N80 Type 1, N80Q, R95 Group 2 M65, L80 Type 1, C90 Type 1, T95 Type 1, C110* Group 3 P110 Group 4 Q125 Type 1

tilly
Download Presentation

API 5CT/ISO 11960 Grades in NACE MR0175/ISO 15156 Pt. 2

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. API 5CT/ISO 11960 Grades inNACE MR0175/ISO 15156 Pt. 2 John W Martin

  2. Listing of API 5CT/ISO 11960 Grades Group 1 H40, J55, K55, N80 Type 1, N80Q, R95 Group 2 M65, L80 Type 1, C90 Type 1, T95 Type 1, C110* Group 3 P110 Group 4 Q125 Type 1 *Not presently covered in NACE MR0175/ISO 15156 Part 2 2

  3. Clause A.2.2.3 NACE MR0175/ISO 15156 Pt. 2 3

  4. Table A.3 NACE MR0175/ISO 15156 Pt. 2 4

  5. Table A.3 NACE MR0175/ISO 15156 Pt. 2 N80Q N80 (Q or type 1) Q125 type 1 R95 Delete year reference (2001) Note b can be deleted 5

  6. Future Work/Ballot How to deal with API 5CT/ISO 11960 Grade C110? This is the closest available. Is it adequate? Can the Grade be listed? Properties of API 5CT/ISO 11960 Grade C110:- • Chemistry – C 0.35 max.; Cr 0.4 to 1.5; Mo 0.25 to 1.00 (e.g. UNS G41350 C 0.33 to 0.38; Cr 0.80 to 1.10; Mo 0.15 to 0.25) • Heat Treatment – Quenched and Tempered (649°C; 1200°F min.) • Yield Strength (range) – 758 to 828 MPa (110 to 120ksi) • Maximum Hardness – 30 HRC 6