1 / 1

A 8-a editie a Seminarului National de Nanostiinta si Nanotehnologie

Tehnica de depunere layer-by-layer pentru obtinerea de nanostructuri hibride Adina Bragaru, Mihaela Miu, Monica Simion, Teodora Ignat, Irina Kleps, Florin Craciunoiu, Veronica Schipu, Adrian Dinescu IMT Bucuresti, 077190, Romania E-mail: adina.bragaru@imt.ro.

waite
Download Presentation

A 8-a editie a Seminarului National de Nanostiinta si Nanotehnologie

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Tehnica de depunere layer-by-layer pentru obtinerea de nanostructuri hibride Adina Bragaru, Mihaela Miu, Monica Simion, Teodora Ignat, Irina Kleps, Florin Craciunoiu, Veronica Schipu, Adrian Dinescu IMT Bucuresti, 077190, Romania E-mail: adina.bragaru@imt.ro Lucrarea prezinta modalitatea in care s-a obtinut un film multistrat de polielectroliti utilizand tehnica layer-by-layer technique (LbL), prin imersia alternativa a membranei de Nafion 117 in solutii de polielectroliti pozitivi si negativi, printr-o procedura ciclica, bazata pe atractia electrostatica dintre polielectrolitii incarcati diferit, poly (sodium styrene sulfonate) - PSS, folosit ca solutie de polianion si respectiv, poly(diallyldimethylammonium chloride)- PDDA – ca solutie de polication. Nafion-ul- un copolimer tetrafluoroetilenic sulfonat cu proprietati ionice, polimer schimbator de cationi, motiv pentru care este folosit ca membrana de electrolit in celulele de combustie. -CF2-CF2- grupe hidrofobe, -SO3H grupare hidrofila si responsabila pentru transportul protonilor Structura Nafion –ului Structura poly (sodium styrene sulfonate) - PSS Structura poly(diallyldimethylammonium chloride)- PDDA Imaginea SEM a suprafetei Nafion –ului Structura schematica a structurii obtinute prin tehnica layer-by-layer pe membrana de Nafion Inainte de a fi utilizata, membrana de Nafion a fost tratata- procedura standard: 30min in solutie 5 % H2O2la 80◦C, apoi 30 min in apa DIla 80◦C si inca 30min in 8% solutie H2SO4 la 80 ◦C. Membrana astfel tratata este imersata pentru 10 minute in solutia de polielectrolit cationic- PDDA si astfel se formeaza la suprafata un strat subtire din acest compus incarcat pozitiv; suprafata obtinuta se va spala dupa care se va imersa in solutie de polielectrolit negativ- PSS, suprafata incarcandu-se astfel negativ. Acest procedeu se va repeta de cateva ori pana cand se va forma un film multistrat de polielectrolit pe membrana de Nafion. Din spectrul IR al membranei de Nafion 117 se disting benzile specifice - 1215 cm-1 si 1147 cm-1 pentru legatura C- F, 1070 cm-1 corespunzatoare intinderii legaturii S-O din grupa SO3H, 980 cm-1 corespunzatoare intinderii legaturii C-F din gruparile CF2-CF(CF3) A 8-a editie a Seminarului National de Nanostiinta si Nanotehnologie 27aprilie 2009, Bucuresti, Romania

More Related