An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Cathode R&D 03/15/06 Saxet project: Bulk GaAs sample #38 (1019cm-3 doping) with 50mm/50mm lines/spacing grid was tested. Lines are 30nm W and 100nm Au. Behavior was different than previous samples Sample with thin GaAs active region and 5×1014cm-3 doping and same grid just arrived. Bulk GaAs samples with W only ~50nm tall lines are coming

  2. Sample #38 I-V curve

  3. Sample #38, QE vs bias

  4. Sample #38, Polarization vs bias

  5. Conclusions • Modeling bias effect on polarization based on Schottky junction formed at the surface if results are encouraging. • We need to investigate the effect of the height of the lines on qe and polarization, i.e. scattering, absorption etc. • An offset Ta cap will be used to investigate the bias distribution at the surface