Growth of All-Metal 3D Photonic Crystals With a Large Infrared Band Gap

Growth of All-Metal 3D Photonic Crystals With a Large Infrared Band Gap. The tungsten 3D photonic crystal was made by selectively removing Si from already fabricated polysilicon/SiO2 structures, and back-filling the resulting mould with chemical vapour deposited (CVD) tungsten.

xiujuan-ye
Download Presentation

Growth of All-Metal 3D Photonic Crystals With a Large Infrared Band Gap

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Growth of All-Metal 3D Photonic Crystals With a Large Infrared Band Gap The tungsten 3D photonic crystal was made by selectively removing Si from already fabricated polysilicon/SiO2 structures, and back-filling the resulting mould with chemical vapour deposited (CVD) tungsten. This method could be extended to create almost any 3D single-crystal metallic photonic crystal at infrared wavelengths; such photonic crystals have not previously been achievable. J.G. Fleming, S. Y.Lin, I. El-Kady, R. Biswas, and K. M. Ho, Nature 417, 52 (2002)

  2. Mid-IR Metallic Layer-by-Layer Photonic Crystals Experimental Transmission, Reflection, and Absorption Spectra Unpolarized Incidence (001) Z Reflection Y Transmission Absorption Wavelength (m ) 4-Layer Tungsten Photonic Crystal a=4.2um, w=1.2um, h=1.5um J.G. Fleming et al., Nature 417, 52 (2002)