1 / 13

A new type Iron-based superconductor ~K 0.8 Fe 2-y Se 2 ~

A new type Iron-based superconductor ~K 0.8 Fe 2-y Se 2 ~. Kitaoka lab Keisuke Yamamoto. D.A.Torchetti et al , PHYSICAL REVIEW B 83 , 104508 (2011 ) W.Bao et al , arXiv:1102.0830v1 Feb (2011). Contents. Introduction Iron-based superconductor History Structure Characteristics

aldis
Download Presentation

A new type Iron-based superconductor ~K 0.8 Fe 2-y Se 2 ~

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. A new type Iron-based superconductor ~K0.8Fe2-ySe2~ Kitaoka lab Keisuke Yamamoto D.A.Torchetti et al , PHYSICAL REVIEW B 83 , 104508 (2011)W.Bao et al , arXiv:1102.0830v1 Feb (2011)

  2. Contents • Introduction • Iron-based superconductor • History • Structure • Characteristics • Experiment ~K0.8Fe2-ySe2~ • Comparison to previous sample • NMR measurement • Summary

  3. Introduction 1900 1920 1940 1960 1980 2000 2020 Year History of superconductivity Discovery of superconducting phenomenon 200 metal heavy fermion system 1911 high-Tc cuprate 163 Hg-Ba-Ca-Cu-O iron-based system under high pressure （ ） 150 Hg-Ba-Ca-Cu-O Tl-Ba-Ca-Cu-O Heavy fermion superconductor 1986 1979 Bi-Sr-Ca-Cu-O 100 Transition temperature (K) Y-Ba-Cu-O 77 High-Tc cuprate superconductor SmO F FeAs 50 0.9 0.11 MgB2 La-Ba-Cu-O LaO F FeAs PuCoGa5 Nb Ge 0.11 0.89 Nb 2006 Pb CeCu2Si2 NbN LaOFeP Hg NbC 0 Iron-based high-Tc superconductor

  4. Introduction Iron-based superconductor 11 system 1111 system 122 system 111 system As Fe-Pnictide layer Fe Se LiFeAs FeSe LaFeAsO BaFe2As2 Tc max = 55K Tc max = 38K Tc max = 8K Tc max = 18K Pnictgen(15族元素)

  5. Introduction Iron-based superconductor Band structure Phase diagram electron hole Fermi suface electron hole nesting

  6. Introduction Iron-based superconductor Regular tetrahedron(109.5°) Nd Dy Pr Er Ba Ce Anion height Fe La α Li Na Pnictgen FeSe

  7. Introduction K0.8Fe2-ySe2 Regular tetrahedron(109.5°) Nd Dy Pr Er Ba Ce K0.8 K0.8 Cs0.8 Cs0.8 La Li Na FeSe J.Guo et al , PHYSICAL REVIEW B 82, 180520R 2010 • Characteristics • isostructural to BaFe2As2 • relatively high Tc of ~33K • heavily electron-doped system

  8. Experiment Fermi surface K0.8Fe2-ySe2 Previous superconductor Band structure Band structure electron hole Qian et al , arXiv:1012.6017v1 Dec (2010) Fermi suface Fermi suface Absence of the hole band electron electron hole hole nesting

  9. Experiment Phase diagram K0.8Fe2-ySe2 Previous superconductor M.Fang et al , EPL, 94 (2011) 27009 TS ,TN≒ 140K~160K TcMAX≒ 50K TS,TN≒300K ~ 500K TcMAX≒ 33K Expect higher Tc AFM:antiferromagnetic(反強磁性) SDW:spin density wave (スピン密度波)

  10. Experiment Ordered state K0.8Fe2-ySe2 Previous superconductor As Fe W.Bao et al , arXiv:1102.0830v1 Feb (2011) • unusual antiferromagnetic structure • Tetragonal（正方晶） • Fe vacancy order • Stripe magnetic order • Orthorhombic（斜方晶） M~0.5μB M~3.31μB

  11. High temperature Low temperature DOS DOS ～kBT（small） ～kBT（large） Experiment E E EF0 EF0 Electron-dope K0.8Fe2-ySe2 D.A.Torchetti et al , PHYSICAL REVIEW B 83 , 104508 (2011) Similar to the electron-doped systems among Fe-based superconductors DOS : density of states

  12. Experiment AFSF(antiferromagnetic spin fluctuation) (Tc~33K) (Tc~9K) • 1/T1T is enhanced toward Tc in both FeSe and the optimally doped Ba(Fe0.92Co0.08)2As2 • enhancement of the AFSF Tc Tc • In K0.8Fe2Se2 , there is no enhancement similarly to overdoped , nonsuperconducting Ba(Fe0.86Co0.14)2As2 (Tc~25K) Tc KxFe2-ySe2 Ba122(OVD) FeSe Ba122(OPT) (Tc~0K) electron Electron dope hole nesting Lack the hole bands near the zone center D.A.Torchetti et al , PHYSICAL REVIEW B 83 , 104508 (2011)

  13. Summary • Introduction about K0.8Fe2-ySe2 • What is the reason of relatively high Tc ? • The structure of Fe-pnictide layer ? • Nesting between electron-band and hole-band ? • High TN and Ts? This sample gives us a new point of view about Iron-based superconductors