1 / 16

KATALITI ČKA KONVERZIJA CO 2 U MOTORNA GORIVA

KATALITI ČKA KONVERZIJA CO 2 U MOTORNA GORIVA. Borivoj Adnađević Fakultet za fizičku hemiju Univerzitet u Beogradu Studentski trg 12-16, 11030 Beograd bora@ffh.bg.ac.rs. Povećanje koncentracije gasova staklene bašte:CH 4 , CO 2 , HCF 3

candra
Download Presentation

KATALITI ČKA KONVERZIJA CO 2 U MOTORNA GORIVA

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. KATALITIČKA KONVERZIJA CO2 U MOTORNA GORIVA Borivoj Adnađević Fakultet za fizičku hemiju Univerzitet u Beogradu Studentski trg 12-16, 11030 Beograd bora@ffh.bg.ac.rs

  2. Povećanje koncentracije gasova staklene bašte:CH4, CO2, HCF3 • Evidentni efekti promene klime:globalno zagrevanje • Ne poštovanje medjunarodnih dogovora: Kjoto protokol • Porast industrijske proizvodnje: trka za profitom • Fotokatalitička redukcija CO2

  3. Tabela 1.: Osnovna fizičkohemijska svojstva ispitivanih fotokatalizatora

  4. Shema 1.: Shema fotokatalitičkog reaktora

  5. Slika 1.: Uticaj vremena ozračivanja na prinos metanola

  6. Tabela 2.: Energetska i kvantna efikasnost ispitivanih fotokatalizatora (Ckat =1%; PCO2=125kPa; CM=2%)

  7. Slika 2.: Uticaj koncentracije M/TiO2 fotokatalizatora na prinos metanola toz =6h; PCO2=125kPa; CM=2%

  8. toz=6h, Ckat. =1% 0.60 0.45 0.30 0.15 0 Slika 3.: Uticaj pritiska CO2 na prinos

  9. Slika 4.: Uticaj koncentracije metanola u katalizatoru naprinos metanola toz =6h; PCO2=125kPa; Ckat =1% CM (%)

  10. Fotoaktivacija TiO2 TiO2 h+ + e- gde je: h+ - šupljina, e- - oslobođeni elektron Oksidacija vode H2O + h+ → •OH + H+ H2O + •OH + 3 h+ → O2 +3 H+ 2 H2O + 4 h+ → O2 +4 H+ gde je: •OH- slobodni OH radikal Redukcija ugljendioksida CO2CO + O2 CO •C + O2 CO2 •C + O2 Formiranje metanola •C + •OH + 3H+ + 3e- → CH3OH

  11. Tabela 3.: Osnovna fizičkohemijska svojstva zeolita HZSM-5 u katalitizatoru KAG-300

  12. Eksperimentalni uslovi Fiksni sloj katalizatora Masa katalizatora m =5 g Vreme reakcije : t=1h Prinos gasne frakcije – volumetrijska metoda Sadržaj C1-C4 ugljovodonika – Gasna hromatografija Prinos H20 i tečnih ugljovodonika –gravimetrijska analiza Sadržaj benzinske frakcije – ASTM-D 3710-83 Sadržaj koksa- ASTM- D- 524

  13. Shema 2: Katalitički reaktor

  14. Tabela 4.: Uticaj temperature na stepen konverzije metanolai raspodelu produkata kataliticke konverzije (P=2MPa; ZB=2 h-1)

  15. Tabela 5.: Uticaj pritiska na stepen konverzije metanola i raspodeluprodukata katalitičke konverzije (T=693K; ZB=2 h-1)

  16. Tabela 6.: Katalitička konverzija C3+C4 frakcije u dizel gorivo (Fiksni sloj katalizatora , mkat= 5g; T=425 K; P=0.41 MPa; ZB= 0.5 h-1)

More Related