Quantum Dot Phosphors for Solid-State Lighting Devices

Quantum Dot Phosphors for Solid-State Lighting Devices. A Report of Preliminary Results Charles P. Gibson, University of Wisconsin Oshkosh. Why Should We be Interested in SSL ?. In the US, 22% of electricity is consumed for lighting. This costs about $50 billion per year.

hasad
Download Presentation

Quantum Dot Phosphors for Solid-State Lighting Devices

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Quantum Dot Phosphors for Solid-State Lighting Devices A Report of Preliminary Results Charles P. Gibson, University of Wisconsin Oshkosh

  2. Why Should We be Interested in SSL ? • In the US, 22% of electricity is consumed for lighting. This costs about $50 billion per year. • High efficiency (>50%) solid-state lighting devices could save up to $42 billion per year. Incandescent efficiency ~ 5% Fluorescent ~ 20% Solid-State (LED) Currently 15 - 30% But could be >50% !

  3. Most SSL Devices Use Light Emitting Diodes. • LEDs are made from inorganic semiconductors. • They contain a p-doped and an n-doped layer. • Application of an electrical bias produces holes (+) and electrons (-). • Recombination of electrons and holes produces light. • Monochromatic light emitted. • Phosphors can be used to create white light. DOE: Basic Research Needs for Solid State Lighting

  4. Most White LEDs Combine Blue and Yellow. • Blue LEDs are used. Some blue light escapes. • Some blue light is captured by a phosphor and is down-converted to yellow. • The combined blue and yellow emission appears to be white. http://www.yfrindia.com/articles/misc/a0098.html

  5. But Color Rendering is a Problem. 485 nm diffuse sunlight 485 nm • Sunlight: High relative intensity across the entire visible region, with a peak in the blue-green region. (CRI = 100) • White LEDs: Narrow blue peak, with broad yellow peak; low intensity in the blue-green region. (CRI ~75) www.mvlc.com

  6. Conventional Approach for Improving CRI. colors. • Use more… • Use assorted LEDs – overly complicated? • Include more phosphors – phosphor development? New Phosphors JNIMS - 2008 Blue LED -SiAlON:Eu CaAlSiN3:Eu 400 nm 500 nm 600 nm 700 nm 800 nm Japan NIMS: 55th Meeting Japan Soc. Applied Physics (2008) http://techon.nikkeibp.co.jp/english/

  7. Alternative Approach: Direct-White Phosphor. • A direct-white phosphor is a single material that emits high-quality white light. • A direct-white phosphor should very broad emission across entire visible region. • A direct-white phosphor should have max in the blue-green region of the spectrum (475 – 525 nm). • Suitable direct-white phosphors for SSL are not available. They need to be developed. Goal: Develop Suitable Direct-White Phosphors.

  8. How About ZnS Quantum Dot Phosphors ? • Desired: Should emit when exposed to near UV light. • ZnS (bulk):Band gap ~3.5 eV (  350 nm). • ZnS (QD): Maybe. May depend on size, composition. • Desired: Good UV-A  visible quantum efficiency. • ZnS (bulk): P22-B  ~ 65%; others may be better. • ZnS (QD): Maybe. May depend on size, composition. • Desired: maxin the blue-green region (475 – 525 nm). • ZnS (bulk): True for many phosphors. • ZnS (QD): Maybe. May depend on size, composition.

  9. How About ZnS Quantum Dot Phosphors ? • Desired: Broad emission, across entire visible range. • ZnS (bulk):Emission bands tend to be rather narrow. • ZnS (QD): Maybe. May depend on size, polydispersity. • Desired: Relatively cheap and easy to make. • ZnS (bulk): Yes. • ZnS (QD): Yes, using arrested precipitation methods. • Desired: Nontoxic. • ZnS (bulk): Relatively nontoxic. • ZnS (QD): Should be relatively nontoxic. (Much less toxic than CdE quantum dots.)

  10. Target Material: Capped ZnS Quantum Dots. Zn salt Mix 1) Purify Activator 2) Cap capped ZnS (QD) phosphor capped ZnS (QD) ZnS (QD) Uncapped QDs Capped QDs Phosphor S source (aq)

  11. First Step: Make Uncapped ZnS QDs. Zn salt Mix 1) Purify Activator 2) Cap capped ZnS (QD) phosphor capped ZnS (QD) ZnS (QD) Uncapped QDs Capped QDs Phosphor S source (aq)

  12. Characterization of Uncapped QDs. • X-ray diffraction confirms ZnS is the product. • Scherrer broadening: ave particle size is ca. 3 – 8 nm. 3 nm ZnS Relative intensity 20 30 40 50 60 70 80 100 90 No emission when irradiated with UV-A (365 nm).

  13. Second Step: Cap the ZnS QDs. Zn salt Mix 1) Purify Activator 2) Cap capped ZnS (QD) phosphor capped ZnS (QD) ZnS (QD) Uncapped QDs Capped QDs Phosphor S source (aq)

  14. ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● Strategy for Capping the Quantum Dots. x x x x ZnS (QD) x x x x - H2S ZnS (QD) + x x O (spacer) X C x x OH x x x x X is a coordinating atom or group

  15. Characterization of Capped QDs. • X-ray diffraction confirms ZnS is the product. • Thermal analysis consistent with monolayer coverage. • XRD and TEM confirm quantum dot size (3 – 8 nm). 5 nm 50 nm No emission when irradiated with UV-A (365 nm).

  16. Third Step: Add Activator. Zn salt Mix 1) Purify Activator 2) Cap capped ZnS (QD) phosphor capped ZnS (QD) ZnS (QD) Uncapped QDs Capped QDs Phosphor S source (aq)

  17. ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● Third Step: Add Activator. x x x x x x Capped ZnS (QD) x x + ZnS (QD) x x x x MLn x x MLn Activator x x

  18. Characterization of Phosphors. • X-ray diffraction confirms ZnS is the product. • XRD and TEM confirm quantum dot size (3 – 8 nm). • Thermal analysis consistent with monolayer coverage. • 0 • Final products glow when irradiated 365 nm. max of emission depends on activator.

  19. Several of the Phosphors are Direct White. 460 nm • max ranges from 440 nm to 500 nm. (Target: 475 – 525 nm.) • Very broad emission in the visible region. • Assymetric peak. (Tail at longer .) • Quantum yield ~10% (No self-absorp. corr.) • No attempt to improve quantum yield. 400 600 nm 500 ZnS(QD):Zn

  20. Emission of ZnS(QD):Zn. • max = 460 nm. Broad peak with tail at longer . • Emission resembles diffuse sunlight in the visible region of the spectrum (400 – 650 nm). 460 nm 485 nm 400 400 600 nm 600 nm 500 500 ZnS(QD):Zn diffuse sunlight

  21. Color Coordinates of ZnS(QD):Zn. • CIE Color coordinates of: direct overhead sunlight: 0.35x, 0.35y • CIE Color coordinates of: ZnS(QD):Zn: 0.29x, 0.33y • CIE Color coordinates of: north sky daylight: 0.30x, 0.31y http://hyperphysics.phy-astr.gsu.edu/hbase/vision/cie.html

  22. Shifting Emission to longer . • Emission can be shifted to longer max by adding Cd2+ as an activator. This gives yellow phosphors. max = 530 542 570 nm ZnS(QD):Cd • max depends on the amount of Cd2+ added.

  23. Conclusions. • We have developed new ZnS quantum dot phosphors. They are relatively cheap and easy to make. • Some of these are direct-white phosphors. When irradiated with UV-A (365 nm), these phoshors have very broad emission. Some of these have max in or close to the desired target range (475 – 525 nm). • The quantum yield for emission of the white phosphors is about 10%. No attempt has been made to optimize quantum yield. • Using Cd2+ as a activator shifts emission to longer wavelength.

  24. Future Work. • Evaluate different capping ligands. Variables: • Length; • Degree of conjugation; • Coordinating groups. • Evaluate different activator. Variables: • Identity of activator; • Amount; • Mixed activators. Example - ZnS(QD):Zn,Cd • Use off the shelf UV-LEDs to construct prototype white SSL devices.

  25. Quantum Dot Phosphors for Solid-State Lighting Devices Preliminary Results: Charles Gibson, UW-Oshkosh Support for this project provided by: UWS-Applied Research Grant Program.

  26. ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● Alternative Embodiment: Transition Layers. The capped/activated quantum dot may include a transition layer of a different semiconductor. x x x x Transition layer in green e.g., ZnO x x x x ZnS (QD) x x x x MLn x x x x

  27. ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● ● Alternative Embodiment: Bridged QDs. x x x x Two or more capped quantum dots may bind to the activator x x x x x x x x ZnS (QD) x x x MLn x x x x x ZnS (QD) x x x x x x x x x x x x

  28. Alternative Embodiment: Bridged QDs. This could result in the formation of oligomers, or 1- 2- or 3-dimensional polymeric networks. Capped QD Capped QD Capped QD MLn MLn MLn x