1 / 23

Lecture 12 – Anisotropic Etching

Lecture 12 – Anisotropic Etching. Anisotropic Etchants & Characteristics Temperature Dependence & Anisotropy Ratio Surface Roughness & Etch Uniformity Masking and Dopant dependence Vertical Sidewalls Corner Compensation Techniques Crystallographic Alignment Patterns.

hea
Download Presentation

Lecture 12 – Anisotropic Etching

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Lecture 12 – Anisotropic Etching • Anisotropic Etchants & Characteristics • Temperature Dependence & Anisotropy Ratio • Surface Roughness & Etch Uniformity • Masking and Dopant dependence • Vertical Sidewalls • Corner Compensation Techniques • Crystallographic Alignment Patterns

  2. Anisotropic Etching Characteristics • Anisotropic etching etches different planes of silicon at different rates • Patterns are bound by the slowest etching plane • Provided more control than that of isotropic wet etching • Pattern transfer with accuracy and reproducibility of 0.5 µm can be achieved • These types of etchants are generally slower than isotropic etchants • class wafers etched around 0.35 µm/min at 63oC • Need elevated temperatures (60-115oC) • Not as sensitive to agitation (although we did some stirring in lab)

  3. Reactant diffuses to the surface Surface reaction Reaction product diffuses away from the surface 1 2 3 Anisotropic Etchants • A wide variety of isotropic etchants have been used • Alkaline aqueous based etchants include KOH, NaOH, LiOH, CsOH, RbOH, NH4OH, and TMAH • Alkaline organics include ethylenediamine (EDP), choline, hydrazine, and sodium silicates • No external voltages are needed for etching • Etching is dopant insensitive over several orders of magnitude • Alcohols (propanol and isopropanol butanol) slow the etching process • The etch rate is reaction rate controlled 1 3 2

  4. Arrhenius Plot for Anisotropic Etching • Etch rate of <100>, <110>, <111> planes of silicon is shown for EDP: • Large temperature dependence • Slope is different for different planes • For EDP, the anisotropy ratio, AR, for (110)/(100)/(111) is smaller than KOH 400/200/1 • Adding organics (IPA) can change the etch rates (hkl)1 etch rate AR = anisotropy ratio =_____________ (hkl)2 etch rate Etch rates for EDP as a function of 1/T

  5. Choosing Anisotropic Etchants Of the main three (KOH, EDP, and TMAH), consider: • Ease of handling • Toxicitiy • Etch rate • Desired topology of the etched bottom surface • Etch stop • Etch selectivity over other materials • Mask material and thickness of mask

  6. Common Anisotropic Etchants KOH (most widely used) • Advantages: Fastest, greatest selectivity, only one that makes vertical sidewalls • Disadvantages: Not CMOS compatible (etches many metals and oxides), alkali ion contamination EDP • Advantages: lots of masks, CMOS compatible, lowest Boron doping etch stop • Disadvantages: toxic corrosive, optically dense (hard to see sample), ages quickly, low AR, and precipitates form during cooling TMAH • Advantages: CMOS compatible, smooth surface • Disadvantages: slow etch rate, poor selectivity (low AR)

  7. Si Surface Roughness • Anisotropic etchants can leave surface roughness behind • Isotropic etchants can be used to touch up the surfaces after anisotropic etching • Macroscopic roughness (notching or pillowing) generally increases with depth but microscopic roughness does not • Average roughness is influenced strongly by fluid agitation, • stirring can reduce roughness magnitudes • ultrasonic agitation can reduce or eliminate it • Average surface roughness (macro and micro) decrease with increasing KOH concentration Macroscopic RoughnessMicroscopic Roughness (variations across 10’s of microns) (variations within a micron) “hillocks” notching

  8. KOH Etch Rate{100}and Uniformity vs Concentration What concentration is etch rate maximal? Where is etch uniformity optimal? Madou, pg 216

  9. KOH Surface Roughness{100}vs Concentration Smoother surfaces are produced by higher or lower concentrations of KOH? Madou pg 216

  10. Etch Rate and Dopant Concentration • High boron concentration drastically reduces the etch rates of silicon • Other impurities also reduce the etch rate but at much higher concentrations • Ion implanted dopants can be used as etch stops • EDP is even more sensitive than KOH to dopant concentrations

  11. Vertical Sidewall Anisotropic Etching • Openings along the <100> direction in {100} silicon with anisotropic etching, etches down at the same rate (equidistant) as it etches under the mask: <110> <100>

  12. Vertical Sidewall – Example 2 <110> <100>

  13. Vertical Sidewall – Example 2 cont

  14. How to Make a Proof Mass • “Interior corners” are not stable when etching with KOH • Pyramidal structures are necessary for proof masses in cantilever pressure sensors and elsewhere. • A decent numerical simulation can be made by assuming only three planes are exposed by KOH etching: {111}, {100}, and {411}

  15. Corner Compensation

  16. {111} & {411} Intersection

  17. Corner Compensation

  18. Corner Compensation

  19. Actual Corner Compensation

  20. Double Square Corner Compensation

  21. Actual Double Square Corner Compensation

  22. <110> Crystallographic Alignment Patterns • “Wagon-wheel” etch mask when anisotropically etched produces a “flower” pattern in {100} Si that • Delineates the {110} directions to better than 0.1° and • Visually depicts the etch ratios between the various crystal planes.

  23. Quotes • Never test the depth of the water with both feet. • Silence is often misinterpreted, but never misquoted. • Laugh every day, it's like inner jogging. • There is no key to happiness. The door is always open. • A grudge is a heavy thing to carry.