Assessment of Carbon Reinforced Composites Irradiation Damage: Weaved Structures Study

This study conducted in 2006 explores the impact of proton irradiation on 2-D and 3-D weaved carbon reinforced composites. The findings indicate both positive and negative effects on the materials, such as self-healing capabilities but also structural degradation at high fluences. Detailed analysis reveals the composite's responses to irradiation exposure and post-exposure annealing, shedding light on the composite's suitability for replacing graphite in high-power beam applications. The study recommends a shift in material selection due to the observed limitations of carbon composites under high fluences.

joannbowen
Download Presentation

Assessment of Carbon Reinforced Composites Irradiation Damage: Weaved Structures Study

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Proton Irradiation Damage Assessmentof Carbon Reinforced Composites: 2-D & 3-D Weaved StructuresA love affair going sour !!! Nick Simos BNL November, 2006

  2. What prompted our love affair with 3D carbon-carbon composite AGS Beam-on-Target tests show clearly that carbon composites are better absorbers of thermo-mechanical shock. This is attributed to the very low coeff. of thermal expansion (CTE). ATJ Graphite 3D CC composite

  3. Positive news regarding 3D Carbon composite kept coming !! Irradiation damage assessment revealed that the composite can undergo self-healing through annealing (even along its 45-degree orientations that form the weak planes) Fiber orientation 45-degree “weak” orientation Good news were associated with modest beam exposure (~ 25,000 uA-hrs). More needed to be done to validate that carbon composites can replace graphite.

  4. Embarked into a 2-phase new study Phase 1Assess the 2D carbon-carbon under heavy irradiation (LHC Phase-I collimator material) Phase 2 Expose 2D & 3D carbon-carbon composites under identical experimental conditions

  5. Phase-1: 2D Carbon Composite In the Spring of 2005 the exact 2-D composite used in the collimator system of LHC was exposed to the BNL BLIP beam. The 2-D composite has a “strong” and a “weak” orientation. The strong orientation is along the reinforcing meshed fibers which form parallel planes. The weak orientation is along the normal to these planes and as s result does not benefit from the presence of reinforcing fibers. The 3-D composite on the other hand has fibers that run normal to the parallel planes. The integrated flux of this exposure was approximately ~3x10^21 protons/cm^2 Integrated beam current ~ 108,000 uA-hrs (at the proton beam 1-sigma  orders of magnitude greater than what the collimator jaw at the LHC is expected to see – nevertheless crucial info for target concepts) Post-irradiation analysis of the exposed 2-D carbon composite revealed both good and bad news: GOOD NEWS: the composite exhibits self-healing behavior (as in the case of the 3-D counterpart) BAD NEWS: Serious structural degradation is observed as a result of high fluences Damage more pronounced along the “weak” orientation

  6. Bad News First: Shown is structural integrity loss (more pronounced in “weak” orientation) “strong” orientation “weak” orientation

  7. Good News: 2D carbon composite exhibits self-healing through thermal annealing (like 3D counterpart) “strong” orientation “weak” orientation Irradiation exposure of different specimens shown in mCi

  8. How well is our nanometer-level analysis controlled/stabilized? Observe the tendency of irradiated 2D carbon (weak orientation) to move away from the expansion trend of the un-irradiated material. Also observe that two specimens at different location within the matrix exposed to similar levels have identical irradiation and post-irradiation (annealing) behavior !!! 4.62 mCi 2.70 mCi 7.62 mCi 8.08 mCi

  9. DILEMMA Is it just the 2D carbon composite that is susceptible to high fluences OR This holds true will ALL carbon composites (2D & 3D) ? The mixed-bag of news prompted us to go through another exposure where 2D and 3D carbon composites are irradiated under same conditions Irradiation of the two carbon composites along with two graphite grades (IG-43 and IG-430) was performed in Spring 2006. Integrated current reached ~ 50,000 uA-hrs (but likely under tighter beam spot!!)

  10. What is the preliminary assessment following irradiation ? Simply put: NOT GOOD !!! Damage to both C-C type is observed ! The integrated current is ~ half of the current achieved during the first exposure of the 2-D carbon composite and yet the damage is as serious. Beam spot measurements at the beginning of the latest round of irradiation and post-irradiation examination of the beam window point towards a tighter beam spot. This will imply that, effectively, the affected material was exposed to similar dose levels. This will soon be verified by detailed examination of beam-registering nickel foils placed within the irradiated assembly True or not, however, the fact remains that serious damage is observed. Establishing the exact threshold when damage is initiated is of limited value and importance at this point !!!

  11. Irradiating beam footprint 2005 Irradiation 2006 Irradiation

  12. Damage seen in the two layers of 3-D carbon composite. Observe the complete disintegration of irradiated specimens situated within the 1-sigma of the beam

  13. Damage seen in the layer of 2-D carbon composite. Severe disintegration of “weakly-oriented” irradiated specimens situated within the 1-sigma of the beam is observed

  14. Where Do We Go from Here? Further experimental scrutiny of 2D or 3D carbon composites for irradiation damage effects is not recommended. These composites clearly CANNOT tolerate the high fluences required by high-power beam targets. These results should prompt a change of course in the search for materials for the multi-MW beam targets. For collimator purposes (such as the LHC) with anticipated fluences far smaller than those experienced during BLIP irradiation, these composites can be viable candidates since they can meet the expansion tolerances toward the beam FOCUS needs to be shifted toward new graphite grades such as IG-430 that are isotropic in their structure (rather than planes that can move relative to each other) Luckily, these graphite grades are part of the latest irradiation phase and their behavior under the same conditions (as those of the carbon composites) will be assessed in the very near term