An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Modifying the crack growth in a glass fiber reinforcedepoxybyadding polyamide 6nanofibres Ives De Baere1,Bert De Schoenmaker2, Sam Van der Heijden2, Wim Van Paepegem1 and Karen De Clerck2 1 MaterialsScience and Engineering Technologiepark-Zwijnaarde 903 9052 Zwijnaarde, Belgium 2 Textiles Technologiepark-Zwijnaarde 907 9052 Zwijnaarde, Belgium

  2. Whythermoplasticnanofibres ? Why nano particles in epoxy resin To improve the mechanical properties PROBLEM: obtaining a homogenous dispersion SOLUTION: thermoplastic nanofibrious structures These can be electrospun, creating a layer of evenly distributed layer of nanofibres Two types are assessed: Directly spun on the glass fabric reinforcement Spun as a separate layer and added in the stacking sequence Influence PA6 nanofibres on mechanical properties – Ives De Baere Faculty of Engineering – EA10 Materials Science and Engineering

  3. PA-6 nanofibres – some properties Non negligible thickness of the nanofibres PA-6 equivalent properties as the matrix Expected improvement of mechanical behaviour ? Influence PA6 nanofibres on mechanical properties – Ives De Baere Faculty of Engineering – EA10 Materials Science and Engineering