Ch 10 Polymer gels

Ch 10 Polymer gels. Physical. Chemical. Rheology of chemical gels. p; the fraction of bonds that are filled. Percolation; the process of network formation by random filling of bonds on a lattice, or by random filling of regions of space. Near equilibrium. for fully cured elastic solid.

mills
Download Presentation

Ch 10 Polymer gels

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Ch 10 Polymer gels

  2. Physical Chemical

  3. Rheology of chemical gels p; the fraction of bonds that are filled Percolation; the process of network formation by random filling of bonds on a lattice, or by random filling of regions of space Near equilibrium for fully cured elastic solid At large deformation Mooney-Rivlin equation

  4. Rheology of partially gelled liquids at the gel point

  5. Time-cure superposition

  6. Rheology of physical gels Physical networks; sticker Associating polymers; water soluble polymers with hydrophobic groups Hydrophilic groups are associating; dipole-dipole interaction in ionomer, hydrogen bonding Attractive interactions promote both gelation and phase separation

  7. Telechelic polymers Linear polymers containing associating sticker groups only on the chain ends HEUR; hydrophobically modified ethoxylated urethanes Ordered cubic array of bridged micelles

  8. Telechelic polymers

  9. Entangled ‘sticky’ chains Many stickers along the chain HASE; hydrophobic alkali-swellable emulsion polymers Shear thickening; caused by a shear-induced change in the balance between intramolecular and intermolecular associations Shear induced gel formation at high shear rates