1 / 31

GAS TURBINE ENGINE JTP FATIGUE TESTING

GAS TURBINE ENGINE JTP FATIGUE TESTING. HCAT Review Meeting 1-2 April 2003 San Diego. SUBSTRATES IN 718 (304) IN901 (184) A286 (136) AM355 (184) 4340(184) 9310 (96) 17-4PH (184). COATINGS (0.003”, 0.015 ”) Bare (Peened/Unpeened) EHC HVOF WC-17Co T-800 T-400 Cr 3 C 2 -20(Ni,Cr)

alexa-armstrong
Download Presentation

GAS TURBINE ENGINE JTP FATIGUE TESTING

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. GAS TURBINE ENGINE JTP FATIGUE TESTING HCAT Review Meeting 1-2 April 2003 San Diego

  2. SUBSTRATES IN 718 (304) IN901 (184) A286 (136) AM355 (184) 4340(184) 9310 (96) 17-4PH (184) COATINGS (0.003”, 0.015”) Bare (Peened/Unpeened) EHC HVOF WC-17Co T-800 T-400 Cr3C2-20(Ni,Cr) Plasma Spray T-400 WC-17Co HVOF/Natural Gas IN718, 4340, AM355 BASIC DoE MATRIX

  3. FATIGUE DoE VARIABLES • Baseline (bare) vs. coating • Peened vs. unpeened (bare only) • Temperature - 300°F vs. 750°F • Dynamic ratio (test type) • A = 0.95 ( control) vs. 0.5 (P control) • R = 0.025 ( control) vs. 0.33 (P control)

  4. 0.5” coating patch

  5. PRELIMINARY COATING BEHAVIOR OBSERVATIONS • EVERYTHING YOU CAN IMAGINE! • +/- FRACTURE PLANE • LOOSE “CIGAR BAND” • MULTIPLE CIRCUMFERENTIAL CRACKS • TOTAL SPALLATION • SOME LONGITUDINAL CRACKS • NO OBVIOUS PATTERN • UNDER PATCH/AT EDGE/OUTSIDE PATCH • TEMPERATURE • COATING TYPE/THICKNESS • SUBSTRATE TYPE

  6. FRACTURE “STATISTICS” LG JTP WAS 4340/300M/A100 AT HRc 52-54

  7. TESTING PROGRESS • 194 individual test groups • 145 coated (75%) • 82 tested (42% of total, 56% of available) • 1276 total test specimens • 988 coated (77%) • 785 tested (60% of total, 80% of coated)

  8. STATUS – GTE FATIGUE PROGRAM • ALL SPECIMENS MANUFACTURED/PEENED FOR ALL PHASES • BARE, EHC, HVOF (WC-Co, T-400, T-800, Cr3C2-20NiCr ), & PS T-400 COATED AND IN TEST • PS WC-Co and HVOF/NATURAL GAS SPECIMENS AVAILABLE • WILL FINISH BY 12/31/03 IF REST OF SPECIMENS ARE COATED SOON