SSL-UCB, ALD MCP Test Progress

SSL-UCB, ALD MCP Test Progress. Sent two MCPs for Al 2 O 3 ALD coating of half surface Both MCPs standard glass MCPs ~ 90Meg Ω. SSL-UCB, ALD MCP Test Progress. The two MCP assemblies were tightened differently, the 12nm sample (left) shows a shadow where the MCP was

hasad
Download Presentation

SSL-UCB, ALD MCP Test Progress

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. SSL-UCB, ALD MCP Test Progress Sent two MCPs for Al2O3 ALD coating of half surface Both MCPs standard glass MCPs ~ 90Meg Ω

  2. SSL-UCB, ALD MCP Test Progress The two MCP assemblies were tightened differently, the 12nm sample (left) shows a shadow where the MCP was clamped in, the 6nm (right) sample shows no deposits at all. The 12nm MCP was a bit loose, and the 6nm was tight.

  3. SSL-UCB, ALD MCP Test Progress ML201-B-2 12nm ALD shows some debris and smudging that was removed in cleaning Before cleaning After cleaning

  4. SSL-UCB, ALD MCP Test Progress ML201-B-1 6nm ALD shows less debris and smudging, - was removed in cleaning Before cleaning After cleaning

  5. Initial Imaging Results on Standard MCPs with 6nm ALD coating Shows definite enhancement of brightness in ALD area No degradation of image quality, except at the boundary zone for coating 1150v MCP, 2800v Screen, UV floodPhotonis ML201-B-1 MCP, 86MΩ 1050v MCP, 2900v Screen, UV floodPhotonis ML201-B-1 MCP, 86MΩ