1 / 38

Classification of Phase Transformations

Classification of Phase Transformations. Functions and discontinuity in differentials. f(x). g(x). h(x). Discontinuity in the curvature. Discontinuity in the slope. g(x). Discontinuity in the function. h(x). f(x). A. Order of a phase transformation. Thermodynamics. Ehrenfest, 1933.

hien
Download Presentation

Classification of Phase Transformations

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript


  1. Classification of Phase Transformations

  2. Functions and discontinuity in differentials f(x) g(x) h(x)

  3. Discontinuity in the curvature Discontinuity in the slope g(x) Discontinuity in the function h(x) f(x)

  4. A Order of a phase transformation Thermodynamics Ehrenfest, 1933 B Classification of Phase Transformations Based on Mechanistic Mechanism Buerger, 1951 C le Chatelier, (Roy 1973) Kinetics

  5. Breaking of bonds and formation of new ones • Atom movements from parent to product by diffusional jumps • Nearest neighbour bonds broken at the transformation front and the product structure is reconstructed by placing the incoming atoms in correct positions → growth of product lattice • Diffusional transformation  Even in case chemical composition same (parent & product) + strict orientation relation → Still lattice correspondence not present • E.g.: Precipitation in Al-Cu alloys • Nucleation of product • Growth Reconstructive Diffusional → Civilian Subset B Replacive → e.g. ordering Mechanistic Buerger, 1951 Displacive Military Cooperative motion of a large number of atoms or a combination Homogenous distortion • E.g.: Martensitic • Formation of nucleus of product • Movement of shear front at speed of sound Shuffling of lattice planes Static displacement wave

  6. Shuffle dominated Lattice strain dominated Magnitude of shuffle and of homogenous lattice strain Presence of precursor mechanical instability Structural basis Displacive Homogenous distortion Shuffling of lattice planes Static displacement wave • Coordination between neighbours retained in the product lattice (though bond angles change) • Atomistic coordination inherited → chemical order in parent structure is fully retained in the product structure similar correspondence of crystallographic planes Lines → lines; planes → planes (vector, plane, unit cell correspondence)  AFFINE TRANSFORMATION In general, an affine transform is composed of linear transformations (rotation, scaling or shear) and a translation (or "shift").

  7. NOTE: Lattice correspondence does NOT imply ORIENTATION RELATION  as phase transformations may involve rigid body rotations

  8. Buerger’s classification: full list • Transformation involving first coordination Reconstructive (sluggish) Dilatational (rapid) • Transformation involving second coordination Reconstructive (sluggish) Displacive (rapid) • Transformations involving disorder  Substitutional (sluggish) Rotational (rapid) • Transformations involving bond type (sluggish)

  9. Non-quenchable Athermal → Rapid C Subset Replacive → e.g. ordering Kinetic le Chatelier, (Roy 1973) Quenchable Thermal → Sluggish * Usually Martensitic transformations are athermal- however there are instances of they being isothermal

  10. A Thermodynamic classification Ehrenfest, 1933 Order of a phase transformation The lowest derivative (n) which shows a discontinuity at the transition point • Can be used for equilibrium transitions of single component systems • There are cases of mixed order transformations • In thermal transformations: usually the high-T form is of higher symmetry and higher disorder

  11. First Order Finite discontinuity n = 1 • First order transitions are characterized by discontinuous changes in entropy, enthalpy & specific volume. • H → change in enthalpy corresponds to the evolution of Latent Heat of transformation • The specific heat [J/K/mole] is thus infinite (i.e. at the transition heat is being put into the system but the temperature is not changing)

  12. Schematics

  13. Finite discontinuity Second Order n = 2 Second derivative is CP • NO discontinuous changes in entropy, enthalpy & specific volume. • NO latent heat of transformation • High specific heat at the transition temperature • Finite discontinuity in CP(NOT infinite) • Lamda () Transitions (-point transitions) show infinity • Concept of a metastable phase not readily applicable to a 2 transition → single continuous free energy curve. • Ferromagnetic ordering, Chemical ordering are examples of 2 transitions. • In a two component system a 2nd order transformation requires equality of entropy and volume of two phases + identical composition of the two phases. Quartz

  14. 2 transitions can be described by mean field descriptions of cooperative phenomenon • Order parameter continuously decreases to zero as T → TC • Any transition which can be described by a continuous change in one or more order parameters can be treated by a the generalized LANDAU Equation

  15. Schematics In a two component system: • 1st order transformation appears in a phase diagram as two line bounding the region where two phases (of different composition) coexist. • Second order transformation appears as a single line. Phase Transformations: Examples from Ti and Zr Alloys, S. Banerjee and P. Mukhopadhyay, Elsevier, Oxford, 2007

  16. Third Order n = 3 • There is usually no classification as third order (II and higher order are clubbed together) • Superconducting transition in tin at zero field & Curie points in many ferromagnets can be considered as third order transitions

  17. Mixed Order

  18. Landau Equation • Close to the critical temperature:The free energy difference (G) between finite and zero values of order parameter () may be expanded as power series • Practically, any physical observable quantity which varies with temperature (or other thermodynamic variable) can be taken as a experimental order parameter A, B, C.. = f(T, P)

  19. First Order n = 1 Not zero Note the barrier • Two minima separated by a G barrier • T slightly less than TC the system still not unstable at  = 0 (state) (curvature remains +ve) a gradual transition of the system in a homogenous fashion to a the free energy minimum at  = C (or near it) is not possible

  20. Phase transition can initiate if localized regions are activated to cross the free energy barrier (beyond  = *) → where phase with finite  can grow spontaneously • Formation of localized product phase regions with  ~ C → nucleation Sharp interface between parent and product phases Nucleation and Growth  Discrete nature of the transformation

  21. Second Order n = 2 • Only even powers • Single equilibrium at  = 0 → corresponds to +ve value of A • +ve curvature • Curvature at  = 0 decreases • System becomes unstable at T = TC and fluctuations will lead to lowering of energy • ve curvature at  = 0→ corresponds to ve value of A • Glass transitions, Paramagnetic-Ferromagnetic transitions

  22. Lambda transitions  • Heat capacity tends to infinity as the transformation temperature is approached • E.g.: Transformation in crystalline quartz Order-disorder transition in -brass (B2 → BCC, Cu-Zn alloy) • Symmetrical -transition → Manganese Bromide Manganese Bromide: Symmetrical -transitions Quartz: Unsymmetrical -transitions

  23. Homogenous (Continuous) Transitions • Parent phase gradually evolves into the product phase without creating a localized sharp change in the thermodynamic properties and structure in any part of the system • The system becomes unstable with respect to small (infinitesimal) fluctuations → leading to the transition • The free energy of the system continuously decreases with amplification of such fluctuations • USUALLY • First order transitions are discrete (For T > Ti )→ Nucleation and Growth • Higher order transitions are homogenous→ parent and product phase cannot be sharply demarcated at any stage of the transition NO Sharp interface between parent and product phases Continuous nature of the transformation

  24. For T < Ti • First order transitions are can proceed in a continuous mode • Not all first order transitions have a instability temperature • Examples of first order continuous transitions (conditions far from equilibrium):Spinodal clusteringSpinodal orderingDisplacement ordering

  25. Spinodal clustering Spinodal decomposition • Phase diagrams showing miscibility gap correspond to solid solutions which exhibit clustering tendency • Within the miscibility gap the decomposition can take place by either  Nucleation and Growth (First order) or by  Spinodal Mechanism (First order) • If the second phase is not coherent with the parent then the region of the spinodal is called the chemical spinodal • If the second phase is coherent with the parent phase then the spinodal mechanism is operative only inside the coherent spinodal domain • As coherent second phases cost additional strain energy to produce (as compared to a incoherent second phase – only interfacial energy involved) → this requires additional undercooling for it to occur

  26. Spinodal decomposition is not limited to systems containing a miscibility gap • Other xamples are in binary solid solutions and glasses • All systems in which GP zones form (e.g.) contain a metastable coherent miscibility gap → THE GP ZONE SOLVUS • Thus at high supersaturations it is GP zones can form by spinodal mechanism

  27. Inverted image (black → white) looks very similar! A coarsened spinodal microstructure in Al-22.5 at.% Zn-0.1 at.% Mg solution treated 2h at 400C and aged 20h at 100C. TEM micrograph at 314 kX. (K.B. Rundman, Metals Handbook, 8th edn. Vol.8, ASM, 1973, p.184.

  28. Spinodal Ordering • Ordering leads to the formation of a superlattice • Ordering can take place in Second Order orFirst Order (in continuous mode below Ti) modes • Any change in the lattice dimensions due to ordering introduces a third order term in the Landau equation • Continuous ordering as a first order transformation requires a finite supercooling below the Coherent Phase Boundary to the Coherent Instability (Ti) boundary • These (continuous ordering) 1st order transitions are possible in cases where the symmetry elements of the ordered structure form a subset of the parent disordered structure Not zero

  29. Liquid Metastable Solid Metastable G → Solid stable Liquid stable Tm METASTABLE STATE For a first order transformation the free energy curve can be extrapolated (beyond the stability of the phase) to obtain a G curve for the metastable state For a second order transformation the free energy curve is a single continuous curve and the concept of a metastable state does not exist

  30. Enantiotropic transformationsEquilibrium transitions: Reversible and governed by classical thermodynamics • L → A (at the melting point: Tm = TL/A) • A → B (at the equilibrium transformation T: TL/A) • A → A’ (transformation between two metastable phases) Monotropic transformationsIrreversible (no equilibrium between parent and product phases) • A’ (metastable) → B (stable) (at T1) • Supercooled liquid(metastable) → A (stable) (at T2)

  31. Displacive transformation • Changes in higher coordination effected by a distortion of the primary bond • Smaller changes in energy • Usually Fast • High temperature form → more open, higher specific volume, specific heat, symmetry • E.g.:  high-low transformations of quartz (843K), tridymite (433K & 378K), cristobalite (523K)  SrTiO3

  32. Toy Model for Displacive Transformation M.J. Buerger, Phase Transformations in Solids, John Wiley, 1951

  33. L +  L  L +  L Ordered solid ’ A B   + ’ Ordered solid ’ A B  + ’

  34. A B L L +  E.g. Au-Ni  2 1 1 + 2