OPTIMALNI REŽIM HLADNOG VALJANJA I ŽARENJA LIMOVA LEGURE TIPA 5083 ZA BRODOGRADNJU

OPTIMALNI REŽIM HLADNOG VALJANJA I ŽARENJA LIMOVA LEGURE TIPA 5083 ZA BRODOGRADNJU. E. Romhanji, M. Popović, D. Glišić, T. Radetić. Tehnološko-metalurški fakultet, Univerzitet u Beograd u. R. Dodok, B. Milović, D. Jovanović. Valjaonica aluminijuma Impol-Seval. Ministarstvo nauke

sani
Download Presentation

OPTIMALNI REŽIM HLADNOG VALJANJA I ŽARENJA LIMOVA LEGURE TIPA 5083 ZA BRODOGRADNJU

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. OPTIMALNI REŽIM HLADNOG VALJANJA I ŽARENJA LIMOVA LEGURE TIPA 5083 ZA BRODOGRADNJU E. Romhanji, M. Popović, D. Glišić, T. Radetić Tehnološko-metalurški fakultet, Univerzitet u Beogradu R. Dodok, B. Milović, D. Jovanović Valjaonica aluminijuma Impol-Seval Ministarstvo nauke Republike Srbije

  2. Pregled Al-Mg legura za brodogradnju Standardne legure Legure nove generacije

  3. Specijalna stanja – H116 i H321 • >3% Mg – osobine i stanja propisana standardom ASTM B 928 • H116 i H321- specijalna stanja Al-Mg legura za primenu u brodogradnji • H116 – deformaciono ojačano stanje • H321 – termički stabilizovano stanje

  4. > 3% Mg povećanje čvrstoće sklonost prema koroziji Optimalni režim hladnog valjanja i žarenja

  5. Materijal • Polazno stanje uzoraka – toplo valjana traka: • 5083 debljina 13,4 mm • 5083+Zn debljina 10,2 mm • 5083+Zn+Zr debljina 11,3 mm • Hladno valjanje do 3,2 mm: • H321 - HV 35%  200°260°C • H116 - HV 18%  250°350°C + 5%zatez.

  6. Ispitivanja • Testovi za ocenu otpornosti prema koroziji: • ASSET - Accelerated Salt Spray Exfoliation Test(ASTM G66) • Osetljivost prema raslojavajućoj koroziji • Rastvor NH4Cl, NH4NO3, amonijum-tartarat, H2O2, t=65°C/24h • NAMLT - Nitric Acid Mass Loss Test(ASTM G67) • Osetljivost prema intergranularnoj koroziji • HNO3 (conc.), t=30°C/24h • m<15mg/cm2  otporan na IG

  7. Osetljivost prema intergranularnoj koroziji 5083 (standardna legura)

  8. 5083 + Zn

  9. 5083 +Zn+Zr

  10. H116 Mehaničke osobine H321

  11. Predlog režima hladnog valjanja H321(osim legure sa Zr) HV 35% + 240C/3h H116 HV 18% + 250°280C/3h + 5% deformacije zatezanjem

  12. H116 Predlog režima prerade legure tipa 5083 H321