1 / 15

UJI KEKERASAN DAN MIKRO STRUKTUR PADA KOMPOSIT AL DAN SiC

UJI KEKERASAN DAN MIKRO STRUKTUR PADA KOMPOSIT AL DAN SiC. Oleh : M . Woko. PENDAHULUAN. Latar Belakang. MATRIK Al + PENGUAT SiC. - Kuat Dan Tahan Aus - Tahan Korosi. BAHAN KONSTRUKSI. INDUSTRI. ALAT-ALAT RUMAH TANGGA. Proses Al + SiC.

kort
Download Presentation

UJI KEKERASAN DAN MIKRO STRUKTUR PADA KOMPOSIT AL DAN SiC

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. UJI KEKERASAN DAN MIKRO STRUKTUR PADA KOMPOSIT AL DAN SiC Oleh: M. Woko

  2. PENDAHULUAN Latar Belakang MATRIK Al + PENGUAT SiC - Kuat Dan Tahan Aus - Tahan Korosi • BAHAN KONSTRUKSI • INDUSTRI • ALAT-ALAT RUMAH TANGGA

  3. Proses Al + SiC • pemrosesan fasa cair (liquid phase processing) squeeze casting • Pemrosesan fasa padat (solid phase processing) (powder metallurgy) FASA Al4C3 1. GETAS 2. TIDAK STABIL PENGGABUNGAN SiC dan Al SULIT *Keterbasahan (wettability) SiCyang rendah * SiC yang mengelompok

  4. TUJUAN • Mengetahui harga kekerasan komposit Al dan SiC • Mengetahui struktur homogenitas komposit Al dan SiC

  5. DASAR TEORI Sifat Fisik Aluminium: • Konduktivitas Listrik Dan Panas Tinggi • Tahan Korosi • Struktur Kristal Kubus (FCC) • Jari-jari 0,14315 nm. • Densitas Rendah 2,699 gr/cm3 • Titik Leleh 660oC • Ringan Tapi Ulet Melebihi Baja BAHAN PADUAN

  6. Sifat Fisik Silicon Carbida (SiC): • Kristalin Hitam Kebiruan • Kekerasan Tinggi • Titik Leleh Tinggi (2837oc) • Kemurnian Tinggi • Tak Berwarna • BA = 40,1 Gr • 70,04% Si DAN 39,06% C • Tidak Larut Dalam Air Dan Pelarut • Kebasahan Rendah Nama Lain: Carborundum Dan Moissanite

  7. METALURGI SERBUK • Keuntungan : • Kecepatan Produk Tinggi • Memiliki Presisi Tinggi • Pemrosessan menggunakan suhu rendah • Keterbatasan : • Mudah Terkontaminasi • Sulit mendapatkan padatan yg merata RETAKAN

  8. Foto SEM, daerah retakan pada komposit isotropik Al/SiC [Siti, 2006]

  9. MATERIAL KOMPOSIT * Penguat memiliki modulus elastisitas yang tinggi * Ada ikatan permukaan yg kuat antara matriks dan penguat KEHOMOGENAN SERBUK Pencampuran : • Proses Kering (dry mixing) • Pencampuran Basah

  10. Pelumasan Mengurangi gaya gesek pada kompresi Penekanan Proses pemadatan pada serbuk Sintering Mengubah partikel tidak stabil menjadi stabil Parameternya: * Temperatur * Kecepatan pemanasan * Waktu * Kecepatan pendinginan

  11. ALAT : 1. Neraca Digital 2. Cetakan sampel 3. Pompa penekan hidrolik 4. Peralatan furnace 5. Gerinda dan pengamplas 6. Magnetik stearer 7. Mikroskop optik BAHAN : Serbuk Al dan SiC Alkohol 96% Zinc Sterat METODOLOGI PENELITIAN

  12. Diagram Alur Percobaan Persiapan bahan uji Pencampuran serbuk Al dan SiC dengan alkohol Pengadukan dan pengeringan Pencetakan Pemanasan Pendinginan Uji Vickers Foto mikrostruktur Penghalusan

  13. HASIL DAN PEMBAHASAN Tabel Hasil Percobaan

  14. Foto Hasil Percobaan Rumus Nilai Kekerasan Nilai kekerasan = 22,23 x 10 x 106 N/mm2 = 222 Mpa. Dengan ralat pengukuran : 0,95 kg/mm2

  15. KESIMPULAN • Diperoleh Aluminium melalui proses metalurgi serbuk dengan harga kekerasan sebesar 222  9,5 MPa. • Ketidak jelasan pengukuran = 4,26% • Taraf Ketelitian = 95,74%.