1 / 27

PINDED JA PINDAMINE

PINDED JA PINDAMINE. Priit Kulu, metalliõpetuse professor TTÜ materjalitehnika instituut. PINDED. Materjali/detaili pinnaomadused(1). Pinnatugevus/kõvadus Kriteeriumid: pinnasiledus (väsimustugevus) jääkpinged pinnakihis (kontaktväsimus)

rasul
Download Presentation

PINDED JA PINDAMINE

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. PINDED JA PINDAMINE Priit Kulu, metalliõpetuse professor TTÜ materjalitehnika instituut

  2. PINDED Materjali/detaili pinnaomadused(1) • Pinnatugevus/kõvadus Kriteeriumid: • pinnasiledus (väsimustugevus) • jääkpinged pinnakihis (kontaktväsimus) • pinnakõvadus: mikro-HV<10N, kriipe- jt. (kulumiskindlus) • Korrosioon - keemiline • elektrokeemiline Kriteeriumid: korrosioonikindlus, kuumuspüsivus, kuumustugevus

  3. PINDED Materjali/detaili pinnaomadused(2) • Kulumine • mehaaniline • korrosiivmehaaniline Kriteeriumid: kulumiskindlus (massi/mahu kaudu, suhteline) • Pindtugevdamise meetodid • kalestamine • pindlegeerimine ja –karastamine • pinded (pihustuspinded, sadestuspinded, sulatuspinded, galvaanpinded, difusioonpinded) • armeerimine (bimetallmaterjalid)

  4. PINDED Süsteem pindematerjal-pindamisprotsess-alusmaterjal PINDEMATERJAL PINDAMISPROTSESS ALUSMATERJAL PINDE OTSTARVE ALUSMATERJALIOMADUSED PINDAMISMOOODUSED Kulumiskindlus Korrosioonikindlus Isoleerivad omadused Elektrilised omadused Optilised omadused Biosobilikkus jt. Mehaanilised Tehnoloogilised Füüsikalised Keemilised Temperatuuri mõju Keemilised Elektrokeemilised Termokeemilised Termopindamine Aurustussadestus Pealekeevitus Plakeerimine jt.

  5. PINDED Tribopinnete struktuur

  6. KEEMILISED ELEKTROKEEMILISED TERMOKEEMILISED TERMOPINDAMINE AURUSTUSSADESTUS MEHAANILISED AlusKasutus Anodeerimine Mg Korrosioon Al Kulumine Fosfaatimine Fe Värvpinde alus Mustamine Fe Korrosioon Kromaatimine Mg Korrosioon Al Värvpinde alus Zn Dekoratiiv PINDED Pindamismoodused(1)

  7. AlusKasutus Nikeldamine Teras Korrosioon - läikiv Cu, Zn, Al Dekoratiiv Plastik Cr aluspinne - must (<5mm) Teras, Cu Korrosioon Dekoratiiv Kroomimine Teras Korrosioon - läikiv Cu, Al Dekoratiiv pluss - kõva kulumine PINDED KEEMILISED ELEKTROKEEMILISED TERMOKEEMILISED TERMOPINDAMINE AURUSTUSSADESTUS MEHAANILISED Pindamismoodused(2)

  8. PINDED KEEMILISED ELEKTROKEEMILISED TERMOKEEMILISED TERMOPINDAMINE AURUSTUSSADESTUS MEHAANILISED AlusKasutus Vasetamine Teras Ag, Ni, värv- Messing pinde alus, Zn-sulamid Jootmine Plastik Tinatamine Al, Cu Jootmine Teras, Malm Tsinkimine Teras, Malm Korrosioon, Cu Värvpinde alus Hõbetamine Teras, Cu, Korrosioon Zn, Ni Pindamismoodused(3)

  9. Kõvakroompinnete kasutus, paksus mm Lõikeriistad 1…5 Mõõteriistad 5…15 Tõmbesilmad ja 5…20 survevormid Plastsurvevaluvormid 5…50 Valtsirullid 50…200 Hüdroseadmete kolvid ja 10…50 silindrid Kuulkraanide kuulid 30…60 Valukokillid 70…400 PINDED KEEMILISED ELEKTROKEEMILISED TERMOKEEMILISED TERMOPINDAMINE AURUSTUSSADESTUS MEHAANILISED Pindamismoodused(4)

  10. Mittemetallid T,oCHRC(HV) Tsementiitimine - gaasiline CO, CH-grupp 900-950 58…62 - tahke BaCO3 HRC Nitriitimine - gaasiline NH3 500-700 450…550 HV - ioon N2 450-580 800…950 HV PINDED KEEMILISED ELEKTROKEEMILISED TERMOKEEMILISED TERMOPINDAMINE AURUSTUSSADESTUS MEHAANILISED Pindamismoodused(5)

  11. PINDED KEEMILISED ELEKTROKEEMILISED TERMOKEEMILISED TERMOPINDAMINE AURUSTUSSADESTUS MEHAANILISED Mittemetallid T,oCHRC(HV) Nitrotsementiitimine - gaasiline CO, 500-750 CH-grupp, NH3 - (vedel) soolad 550-950 Si, B Metallid Kroomimine FeCr Kulumine 1000… Alumiinimine FeAl 1100 Kuumus- püsivus Pindamismoodused(6)

  12. Protsessid TKT-l Dissotsiatsioon (monoelemendi teke) 2COg CO2+Ci 2 NH3g3H2+3Ni FeCr+4NH4ClgFeCl4+Cr+2N2+4H2 Adsorbtsioon (lahutumine) Difusioon Kihi koostissügavus Cg1,5% dg1,5 mm Crg30% dg0,5 mm Alg40%dg0,8mm PINDED KEEMILISED ELEKTROKEEMILISED TERMOKEEMILISED TERMOPINDAMINE AURUSTUSSADESTUS MEHAANILISED Pindamismoodused(7)

  13. Põlemisel põhinevad - leek - detonatsioon - kiirleek (HVAF/HVOF) Elektrilised - kaar - plasma - laser PINDED KEEMILISED ELEKTROKEEMILISED TERMOKEEMILISED TERMOPINDAMINE AURUSTUSSADESTUS MEHAANILISED Pindamismoodused(8)

  14. PINDED Pihustuspindamine Pinde struktuur Kiiruse ja temperatuuri mõju

  15. PINDED Pihustuspindematerjalid Metallid Mittemetallid Intermetalliidid Kõvamaterjalid Karbiid- ja nitriid- keraamika: WC, TiN jt. Oksiidkeraamika Al2O3, TiO2 jt. Metallid Sulamid Kermised Kõvad sulamid PINNE

  16. PINDED Pindamismoodused(9) • KEEMILISED • ELEKTROKEEMILISED • TERMOKEEMILISED • TERMOPINDAMINE • AURUSTUSSADESTUS • MEHAANILISED

  17. PINDED PVD PVD põhimõte Plasmanitriitimine 1- katood 2, 3- kiirendid 4- anood 1- ioonplasma 2- anood 3- pinnatav detail

  18. PINDED PVD võimalused • KEEMILISED • ELEKTROKEEMILISED • TERMOKEEMILISED • TERMOPINDAMINE • AURUSTUSSADESTUS • MEHAANILISED

  19. PINDED PVD pinnete struktuur • KEEMILISED • ELEKTROKEEMILISED • TERMOKEEMILISED • TERMOPINDAMINE • AURUSTUSSADESTUS • MEHAANILISED

  20. PINDED CVD põhimõte • KEEMILISED • ELEKTROKEEMILISED • TERMOKEEMILISED • TERMOPINDAMINE • AURUSTUSSADESTUS • MEHAANILISED

  21. PINDED PVD ja CVD temperatuur ja pinde paksus • KEEMILISED • ELEKTROKEEMILISED • TERMOKEEMILISED • TERMOPINDAMINE • AURUSTUSSADESTUS • MEHAANILISED

  22. PINDED PVD ja CVD pinnete kasutus • KEEMILISED • ELEKTROKEEMILISED • TERMOKEEMILISED • TERMOPINDAMINE • AURUSTUSSADESTUS • MEHAANILISED

  23. PINDED Pindamismoodused(10) Valtsimine Lehtmaterjal valtsitakse alusele g difusioonlõõmutus, d =1…20 mm Kuumpressimine Järgneb külmvaltsimine Rullkeevitus Elektrkontaktkeevitus, d al. 50 mm Plahvatuspindamine Sherardeerimine Detailid pöörlevas trumlis koos klaaskuulide, Zn, Al jt. pulbritega toatemperatuuril 400-500 oC (difusioonpindamine) • KEEMILISED • ELEKTROKEEMILISED • TERMOKEEMILISED • TERMOPINDAMINE • AURUSTUSSADESTUS • MEHAANILISED

  24. PINDED Pinnete kasutus(1)Terased Materjal Tarbimisom.

  25. PINDED Pinnete kasutus(2)Terased Materjal Tarbimisom.

  26. PINDED Pinnete kasutus(3)Sulamid Materjal Tarbimisom.

  27. PINDED Pinnete kasutus(4)Sulamid Materjal Tarbimisom.