AÇO INOXIDÁVEL DUPLEX: CARACTERÍSTICAS DE FABRICAÇÃO E UTILIZAÇÃO

AÇO INOXIDÁVEL DUPLEX: CARACTERÍSTICAS DE FABRICAÇÃO E UTILIZAÇÃO. Dr. Eng. SERGIO MAZZER ROSSITTI (1) Eng. MAURO MAZZER ROSSITTI (2) (1)(2) GRUPOMETAL LTDA –AÇO INOXIDÁVEL E LIGAS ESPECIAIS. HISTÓRICO. Aços Inoxidáveis – descobertos início século XX 1912 – austeníticos e martensíticos

Audrey
Download Presentation

AÇO INOXIDÁVEL DUPLEX: CARACTERÍSTICAS DE FABRICAÇÃO E UTILIZAÇÃO

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. AÇO INOXIDÁVEL DUPLEX: CARACTERÍSTICAS DE FABRICAÇÃO E UTILIZAÇÃO Dr. Eng. SERGIO MAZZER ROSSITTI (1) Eng. MAURO MAZZER ROSSITTI (2) (1)(2) GRUPOMETAL LTDA –AÇO INOXIDÁVEL E LIGAS ESPECIAIS

  2. HISTÓRICO • Aços Inoxidáveis – descobertos início século XX • 1912 – austeníticos e martensíticos • 1920 – ferríticos • 1927 – duplex • BRASIL • Início de utilização – só nos anos 80 (desconhecimento + dificuldades na fabricação) • Ainda não fabrica chapas de duplex

  3. PROPRIEDADES • O que é um Aço inoxidável Duplex? • Microestrutura Duplex constituída por duas fases em proporções aproximadamente iguais • Ferrita () + Austenita ( ) • Superduplex? • PREn = Pitting Resistance Equivalent number • PREn = %Crlivre + 3,3(%Mo +0,5%W) + 2(%Cu) +16(%N) sendo Crlivre = %Cr - 14,5(%C) • PREn > 40 = Superduplex

  4. PROPRIEDADES

  5. PROPRIEDADES • Propriedades Mecânicas • LE > 450 MPa • impacto > 55 J (T ambiente) • Fabricação • boa fundibilidade • excelente soldabilidade • média usinabilidade • Resistente à Corrosão • por pite e fresta • intercristalina • sob tensão induzida por cloretos

  6. APLICAÇÃO - Produtos

  7. ÁREAS DE APLICAÇÃO OFF SHORE: CL- H2S Ph<4 altas velocidades de bombeamento

  8. ÁREAS DE APLICAÇÃO Customer: PETROBRÁS Power: 3287 HP Pump Type: GSG 150-360 1+5 Total Weight: 160 tons Dimensions (total): - Length: 16 m (52,5 ft) - Width: 7 m (23 ft) - Height: 4,2 m (14 ft) Fluid: Sea Water Flow: 445 m3/h (1958 USGPM) Head: 1454 m (4770 ft)

  9. ÁREAS DE APLICAÇÃO Customer: RIPASA/SP - Papel Celulose Pump Type: NCH-300-350 Application: residual water extraction Flow: 1200 m3/h Head: 24 m Power: 150 HP

  10. FABRICAÇÃO • Diferença fundamental : presença de fases intermetálicas (principal fase )

  11. Processo de fabricação de pecas fundidas em duplexEtapas

  12. FABRICAÇÃO - Elaboração da Liga

  13. FABRICAÇÃO - Rebarbação - Corte de Canais Microestrutura repleta de fase  - frágil

  14. FABRICAÇÃO - Microestruturas no estado bruto de fundição

  15. FABRICAÇÃO - Corte de Canais

  16. FABRICAÇÃO – Tratamento térmico

  17. FABRICAÇÃO – Tratamento térmico

  18. FABRICAÇÃO – Solda

  19. CONSIDERAÇÕES FINAIS • Em função das propriedades, o consumo de duplex e superduplex vai aumentar • Fabricação destes aços exige conhecimento aprofundado de metalurgia • Só atender à norma de AQ e PM não garante desempenho do material • Devem ser considerados a experiência e o histórico de fornecimento do fundidor