Caracterização da Composição de um Material Vítreo obtido a partir da Fosforita Natural utilizando o ED-XRF e o WD-XRF. Nomes N°. USP Juliana P. de Souza 6435232 Rodrigo P. de Almeida 5609971. INTRODUÇÃO.

harlow
Download Presentation

Nomes N°. USP Juliana P. de Souza 6435232

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. Caracterização da Composição de um Material Vítreo obtido a partir da Fosforita Natural utilizando o ED-XRF e o WD-XRF Nomes N°. USP Juliana P. de Souza 6435232 Rodrigo P. de Almeida 5609971

  2. INTRODUÇÃO Vidros são sólidos amorfos, que apresentam viscosidade maior que 1013 poise à temperatura ambiente e átomos localizados em posições desordenadas e apresentam relaxamento estrutural.

  3. INTRODUÇÃO Os Raios X são radiações eletromagnéticas de comprimento de onda entre 0,1-100 Å (Angstron) e é emitido pela desaceleração de elétrons ou por transições de elétrons de um nível energético maior para um menor.

  4. OBJETIVOS Estudar a compatibilidade entre as medidas realizadas por um ED-XRF e um WD-XRF de varias amostras de um material obtido a partir da rocha fosforita natural e do fosfato de sódio P.A (NaH2PO4).

  5. MATERIAIS E MÉTODOSProdução • Composições de 50% NaH2PO4 e 50% de fosforita e 67% NaH2PO4 e 33% fosforita. • Levadas ao forno de 100°C a 1100°C. • Vertidas em água (fritas), ou fôrmas de aço (em seguida com o processo de recozimento).

  6. MATERIAIS E MÉTODOSPreparação • Amostras moídas para reduzir a granulometria. • Prensadas a 10toneladas/10mm durante 5s.

  7. MATERIAIS E MÉTODOSMedidas

  8. RESULTADOS

  9. DISCUSSÃO

  10. CONCLUSÃO

  11. REFERÊNCIAS BIBLIOGRÁFICAS [1] PAUL, A. Chemistry of glasses. 1. ed. New York, N.Y.: Chapman and Hall, 1982. [2] Navarro, J.M.F. El vidrio. 2.ed. Madrid, Espanha: C.S.I.C., 1991. [3] VAN WAZER, J.R. Phosphorus and its compounds. v. 1, New York, Interscienc, 1958. [4] Peng, Y.B.; Day, D.E. High thermal expansion phosphate glasses. Glass Technology. v. 32, p. 166-173, 1991. [5] El-Ati, M.I.; Higazy, A.A. Electrical conductivity and optical properties of gamma-irradiated niobium phosphate glasses. J. Mat. Sci., v. 35, p. 6175 – 6180, 2000. [6] Sales, B.C., Boatner, L.A. Lead-Iron Phosphate Glass: A Stable Storage Medium for High-Level Nuclear Waste. Science, v. 226, p. 45-48, 1984. [7] Donald, I.W. Preparation, properties and chemistry of glass- and glass-ceramic-to-metal seals and coatings. J. Mat. Sci. v. 28, p 2841-2286, 1993. [8] Anvari, S.F.; Hogarth, C.A.; Moridi, G.R. Electrical Conductivity of Zinc-Barium Phosphate Glasses. J. Mat. Sci.v. 26, p. 3639-3642, 1991. [9] PYARE, R. Leachability of zinc ions from ternary phosphate glasses. J. Mat. Sci., v. 38, p 2079-2086, 2003. [10] REIS, S.T. Durabilidade química de vidros sinterizados à base de fosfato de ferro e chumbo. 1999. Tese (Doutorado) - Instituto de Pesquisas Energéticas e Nucleares, São Paulo. [11] ARANHA, N.Vidros niobofosfatos: preparação, caracterização e propriedades. 1994. Tese (Doutorado) – Universidade Estadual de Campinas, Campinas. [12] SALVADOR, V.L.R. Espectrometria de Fluorescência de Raios X – (IPN-0014). 2010. [13] RIBAS, R.V. Estrutura da Matéria-I (notas de aula). 14 de maio de 2009.