PELEBURAN LOGAM NON-BESI Pertemuan 3

PELEBURAN LOGAM NON-BESI Pertemuan 3. Matakuliah : D0234 - Teknologi Proses Tahun : 2007. Learning Outcomes. Mahasiswa dapat menerangkan cara pengolahan logam non-besi. Outline Materi :. Karakteristik Umum Logam Non-besi Tahap Peleburan Proses Pembuatan Logam Non-besi

monet
Download Presentation

PELEBURAN LOGAM NON-BESI Pertemuan 3

An Image/Link below is provided (as is) to download presentation Download Policy: Content on the Website is provided to you AS IS for your information and personal use and may not be sold / licensed / shared on other websites without getting consent from its author. Content is provided to you AS IS for your information and personal use only. Download presentation by click this link. While downloading, if for some reason you are not able to download a presentation, the publisher may have deleted the file from their server. During download, if you can't get a presentation, the file might be deleted by the publisher.

E N D

Presentation Transcript

  1. PELEBURAN LOGAM NON-BESIPertemuan 3 Matakuliah : D0234 - Teknologi Proses Tahun : 2007

  2. Learning Outcomes . Mahasiswa dapat menerangkan cara pengolahan logam non-besi Outline Materi : • Karakteristik Umum Logam Non-besi • Tahap Peleburan • Proses Pembuatan Logam Non-besi • Pengecoran Logam Non-besi

  3. KARAKTERISTIK UMUM LOGAM NON-BESI • Memiliki berat jenis lebih kecil daripada logam besi, • kecuali Pb, Ni, Cu dan paduannya; • Pada umumnya tahan terhadap korosi (air atau • kelembaban); • Memiliki nilai estetika yang tinggi (warna yang menarik); • Pada umumnya memiliki daya hantar listrik yang baik • (Al, Cu, Pt, dll.); • Pada umumnya memiliki titik lebur lebih rendah daripada • logam besi; • Pada umumnya sulit dilas.

  4. TAHAPPELEBURAN • Tahap penghalusan mineral, • Tahap pencucian, • Tahap pemisahan antara logam dan kotoran, dan • Tahap peleburan. PROSES PEMBUATAN LOGAM NON-BESI • Pembuatan Aluminium, • Pembuatan Magnesium, • Pembuatan Tembaga, dan • Pembuatan Timah Hitam.

  5. Pembuatan Aluminium • Proses Bayern : Figure 3.1 Electrolytic in pot room of aluminium reduction plant

  6. Mg(OH)2 HCl MgCl2 Mg(OH) 2 + 2HCl MgCl2 +2H2O Pembuatan Magnesium • Proses pembuatan magnesium dari air laut : Figure 3.2 Manufacture flow process chart for magnesium from seawater

  7. Pembuatan Tembaga • Proses peleburan tembaga : Kalsin = CuS, FeO, SiO2, dan CuS Figure 3.3 Manufacture flow process chart for copper smelting by the reverberatoty converter process

  8. Pembuatan Timah Hitam • Proses pembuatan timah hitam : Figure 3.4 Manufacture flow process chart for producing lead

  9. PENGECORAN LOGAM NON-BESI Cara pengecoran hampir sama dengan logam besi, dengan sedikit perbedaan: • Cetakan umumnya dibuat dengan cara dan alat yang • sama dengan logam besi, • Pasir cetak harus lebih halus, karena benda cetak • umumnya lebih kecil dan biasanya diinginkan permukaan • yang rata; • Pasir tidak perlu tahan panas yang tinggi karena suhu • pengecoran lebih rendah; • Perpaduan dilakukan dengan menambahkan unsur-unsur • tertentu dengan tepat pada logam dasar.

  10. Jenis dapur peleburan logam non-besi : • Dapur kowi dengan sumber energi panas kokas, minyak, • atau gas (lihat Figure 2.3); • Bila dibutuhkan pengendalian suhu yang cermat dapat • digunakan : - dapur tahanan listrik, - dapur busur tak langsung, atau - dapur induksi (lihat Figure 2.7).

  11. Figure 2.7 Induction furnace Figure 2.8 Oil-or gas-fired tiling crucible furnace • Induksi • Krusibel

  12. SELESAI TERIMA KASIH