Work Report. GengYaochen Sept.14th. Effect of Ce addition. adjust Ce content of catalyst to abtain different ratio of Cu + /Cu 0 after reduction and correlate the ratio with C DMO &S EG data to figure out the role that Cu + & Cu 0 play in the reaction.
E N D
Work Report GengYaochen Sept.14th
Effect of Ce addition adjust Ce content of catalyst toabtain different ratio of Cu+/Cu0 after reduction and correlate the ratio with CDMO &SEG data to figure out the rolethat Cu+&Cu0play in the reaction
Cu(NO3)2+ Ce(NO3)3 + ammonia 真空 干燥 硅溶胶 搅拌 80℃ 蒸氨 抽滤 洗涤 400℃ 焙烧 Catalysts preparation Ammonia Evaporation Method ICP analysis
Characterization N2O Titration • Metal dispersion diminishes along with the increase of Ce • content in the catalyst, which indicates that the Cu0 on the • surface decreases.
Characterization TPR Intensity (a.u.) 1.2Ce 1Ce 0.8Ce 0.6Ce 100 120 140 160 180 200 220 240 260 280 300 Temperature (℃)
Characterization BET analysis
Characterization 1.2Ce dV/dD (cm3g-1nm-1) 1Ce 0.8Ce 0.6Ce Pore Diameter (nm)
Characterization XRD ♦ Cu+ ♦ ▼ Cu0 ▼ ▼ ▼ 1.2Ce Intensity (a.u.) 1Ce 0.8Ce 0.6Ce 2 Theta (degree)
Characterization N2O Titration ? • Metal dispersion diminishes along with the increase of Ce • content in the catalyst, which indicates that the Cu0 on the • surface decreases. • The Ce contents of catalysts are so close that the real • regularity is blanketed by experimental errors.
Thanks for your attention! Qs & As